Friction Stir Welding of Zr55Al10Ni5Cu30 Bulk Metallic Glass to Crystalline Aluminum

J Mater Sci Technol ›› 2009, Vol. 25 ›› Issue (06): 853-856.

• Articles • Previous Articles Next Articles

Friction Stir Welding of Zr55Al10Ni5Cu30 Bulk Metallic Glass to Crystalline Aluminum

Zuoxiang Qin¹⁾, Cuihong Li¹⁾, Haifeng Zhang¹⁾, Zhongguang Wang¹⁾, Zhuangqi Hu¹⁾, Zhiqiang Liu²⁾

1) Shenyang National Laboratory for Materials Science, Institute of Metal Research, Chinese Academic of Sciences, Shenyang 110016, China
2) School of Materials Science and Engineering, Dalian Jiaotong University, Dalian 116028, China

Received:2008-03-20 Revised:2008-06-03 Online:2009-11-28 Published:2009-11-24
Contact: Zuoxiang Qin
Supported by:
the Ministry of Science and Technology of China (Grant No. 2006CB605201)
the National Natural Science Foundation of China (Grant Nos. 50825402 and 50731005)

Abstract

Abstract:

The Zr₅₅Al₁₀Ni₅Cu₃₀bulk metallic glass plate were successfully welded to crystalline aluminum plates by using a friction stir welding (FSW) method. The welded zone was examined. No defects, cracks or pores were observed and no other crystalline phases except for aluminum were found in the welded joint. The strength of the joint is higher than that of aluminum. The glassy phase in the stir zone keeps the amorphous state, showing a successful welding. The storage modulus softens over the glass transition. And the weldability was discussed according to this phenomena.

Key words: Bulk metallic glass, Zr-based alloy, Friction stir welding

Zuoxiang Qin,Cuihong Li,Haifeng Zhang,Zhongguang Wang,Zhuangqi Hu,Zhiqiang Liu. Friction Stir Welding of Zr55Al10Ni5Cu30 Bulk Metallic Glass to Crystalline Aluminum[J]. J Mater Sci Technol, 2009, 25(06): 853-856.

References

[1 ] W.L. Johnson: Curr. Opin. Solid State Mat. Sci., 1996, 3, 383.
[2 ] A. Inoue: Bulk Amorphous Alloys Preparation and Fundamental Characteristics, Trans. Tech. Publications, ZÄurich, 1998, Ch. 1.
[3 ] A. Inoue: Acta Mater., 2000, 48, 279.
[4 ] W.H. Wang, C. Dong and C.H. Shek: Mater. Sci. Eng. R, 2004, 44, 45.
[5 ] A. Inoue, B. Shen and N. Nishiyama: Bulk Metallic Glasses, eds M. Miller and P. Liaw, Springer, New York, 2007, Ch. 1.
[6 ] Y. Kawamura, T. Nakamura, A. Inoue and T. Masumoto: Mater. Trans., JIM, 1999, 40, 794.
[7 ] Y. Kawamura, T. Shibata, A. Inoue and T. Masumoto: Scripta Mater., 1997, 37, 431.
[8 ] Y. Kawamura, T. Nakamura and A. Inoue: Scripta Mater., 1998, 39, 301.
[9 ] Y. Kawamura, T. Shibata, A. Inoue and T. Masumoto: Acta Mater., 1998, 37, 253.
[10] Y. Kawamura, Y. Ohno and A. Chiba: Mater. Sci. Forum, 2002, 386-388, 553.
[11] Y. Kawamura and Y. Ohno: Scripta Mater., 2001, 45, 127.
[12] Y. Kawamura and Y. Ohno: Mater. Trans., 2001, 42, 2476.
[13] S. Kagao, Y. Kawamura and Y. Ohno: Mater. Sci. Eng. A, 2004, 375-377, 312.
[14] J. Kim and Y. Kawamura: Scripta Mater., 2007, 56, 709.
[15] B. Li, Z.Y. Li, J.G. Xiong, L. Xing and Y. Li: J. Alloy. Compd., 2006, 413, 118.
[16] J.H. Kim, C. Lee, D.M. Lee, J.H. Sun, S.Y. Shin and J.C. Bae: Mater. Sci. Eng. A, 2007, 449, 872.
[17] Y. Kawamura and Y. Ohno: Scripta Mater., 2001, 45, 279.
[18] T. Shoji, Y. Kawamura and Y. Ohno: Mater. Trans., 2003, 44, 1809.
[19] C.H. Wong and C.H. Shek: Scripta Mater., 2003, 49, 393.
[20] T. Shoji, Y. Kawamura and Y. Ohno: Mater. Sci. Eng. A, 2004, 375, 394.
[21] Y. Kawamura: Mater. Sci. Eng. A, 2004, 375-377, 112.
[22] M. Guerra, C. Schmidt, J.C. McClure, L.E. Murr and A.C. Nunes: Mater. Trans., 2003, 49, 95.
[23] R.S. Mishra and Z.Y. Ma: Mater. Sci. Eng. R, 2005, 50, 1.
[24] L.E. Murr, Y. Li, R.D. Flores, E.A. Trillo and J.C. McClure: Mater. Res. Innov., 1998, 2, 150
[25] X.L. Su, K.S. Wang and J.J. Zhou: Weld. Technol., 2006, 35(1), 12. (in Chinese)

[1]	L. Deng, K. Kosiba, R. Limbach, L. Wondraczek, U. Kühn, S. Pauly. Plastic deformation of a Zr-based bulk metallic glass fabricated by selective laser melting [J]. J. Mater. Sci. Technol., 2021, 60(0): 139-146.
[2]	W. Zhai, L.H. Nie, X.D. Hui, Y. Xiao, T. Wang, B. Wei. Ultrasonic excitation induced nanocrystallization and toughening of Zr_46.75Cu_46.75Al_6.5 bulk metallic glass [J]. J. Mater. Sci. Technol., 2020, 45(0): 157-161.
[3]	Weijie Ren, Dejia Liu, Qing Liu, Renlong Xin. Influence of texture distribution in magnesium welds on their non-uniform mechanical behavior: A CPFEM study [J]. J. Mater. Sci. Technol., 2020, 46(0): 168-176.
[4]	Mariana X. Milagre, Uyime Donatus, Naga V. Mogili, Rejane Maria P. Silva, Bárbara Victória G. de Viveiros, Victor F. Pereira, Renato A. Antunes, Caruline S.C. Machado, João Victor S. Araujo, Isolda Costa. Galvanic and asymmetry effects on the local electrochemical behavior of the 2098-T351 alloy welded by friction stir welding [J]. J. Mater. Sci. Technol., 2020, 45(0): 162-175.
[5]	Zhiqiang Zhang, Changshu He, Ying Li, Lei Yu, Su Zhao, Xiang Zhao. Effects of ultrasonic assisted friction stir welding on flow behavior, microstructure and mechanical properties of 7N01-T4 aluminum alloy joints [J]. J. Mater. Sci. Technol., 2020, 43(0): 1-13.
[6]	Wei Hu, Zhongwei Ma, Shude Ji, Qi Song, Mingfei Chen, Wenhui Jiang. Improving the mechanical property of dissimilar Al/Mg hybrid friction stir welding joint by PIO-ANN [J]. J. Mater. Sci. Technol., 2020, 53(0): 41-52.
[7]	Longjun Wu, Zhengwang Zhu, Dingming Liu, Huameng Fu, Hong Li, Aimin Wang, Hongwei Zhang, Zhengkun Li, Long Zhang, Haifeng Zhang. Deformation behavior of a TiZr-based metallic glass composite containing dendrites in the supercooled liquid region [J]. J. Mater. Sci. Technol., 2020, 37(0): 64-70.
[8]	Yanhui Li, Siwen Wang, Xuewei Wang, Meiling Yin, Wei Zhang. New FeNiCrMo(P, C, B) high-entropy bulk metallic glasses with unusual thermal stability and corrosion resistance [J]. J. Mater. Sci. Technol., 2020, 43(0): 32-39.
[9]	S.C. Han, L.H. Wu, C.Y. Jiang, N. Li, C.L. Jia, P. Xue, H. Zhang, H.B. Zhao, D.R. Ni, B.L. Xiao, Z.Y. Ma. Achieving a strong polypropylene/aluminum alloy friction spot joint via a surface laser processing pretreatment [J]. J. Mater. Sci. Technol., 2020, 50(0): 103-114.
[10]	C. Yang, J.F. Zhang, G.N. Ma, L.H. Wu, X.M. Zhang, G.Z. He, P. Xue, D.R. Ni, B.L. Xiao, K.S. Wang, Z.Y. Ma. Microstructure and mechanical properties of double-side friction stir welded 6082Al ultra-thick plates [J]. J. Mater. Sci. Technol., 2020, 41(0): 105-116.
[11]	Haichao Sun, Zhiliang Ning, Jingli Ren, Weizhong Liang, Yongjiang Huang, Jianfei Sun, Xiang Xue, Gang Wang. Serration and shear avalanches in a ZrCu based bulk metallic glass composite in different loading methods [J]. J. Mater. Sci. Technol., 2019, 35(9): 2079-2085.
[12]	Yongxian Huang, Yuming Xie, Xiangchen Meng, Junchen Li, Li Zhou. Joint formation mechanism of high depth-to-width ratio friction stir welding [J]. J. Mater. Sci. Technol., 2019, 35(7): 1261-1269.
[13]	H. Zhang, P. Xue, D. Wang, L.H. Wu, D.R. Ni, B.L. Xiao, Z.Y. Ma. Effect of heat-input on pitting corrosion behavior of friction stir welded high nitrogen stainless steel [J]. J. Mater. Sci. Technol., 2019, 35(7): 1278-1283.
[14]	X.C. Liu, Y.F. Sun, T. Nagira, K. Ushioda, H. Fujii. Evaluation of dynamic development of grain structure during friction stir welding of pure copper using a quasi in situ method [J]. J. Mater. Sci. Technol., 2019, 35(7): 1412-1421.
[15]	X.H. Zeng, P. Xue, L.H. Wu, D.R. Ni, B.L. Xiao, K.S. Wang, Z.Y. Ma. Microstructural evolution of aluminum alloy during friction stir welding under different tool rotation rates and cooling conditions [J]. J. Mater. Sci. Technol., 2019, 35(6): 972-981.

Friction Stir Welding of Zr55Al10Ni5Cu30 Bulk Metallic Glass to Crystalline Aluminum

RichHTML

PDF (PC)

Knowledge

Abstract

Cite this article

share this article

References

Related Articles 15

Recommended Articles

Metrics

Comments