Corrosion of AISI 4130 Steel Alloy under Hydrodynamic Condition in Ethylene Glycol+ Water+NO2-­­­­ Solution

doi:10.1016/j.jmst.2012.11.013

Abstract

Abstract:

The electrochemical behavior of steel alloy in ethylene glycol–water mixture at different solution rotating speeds was investigated by polarization curves and AC impedance measurements (EIS). The results obtained showed that corrosion rate was not changed significantly at different rotating speeds and was decreased with increasing ethylene glycol concentration. The effect of nitrite as an inhibitor was studied and high inhibition efficiency was obtained. It was found that surface passivation occurred in the presence of inhibitor. The inhibiting effect of the nitrite was explained on the basis of the competitive adsorption between the inorganic anions and the aggressive Cl⁻ ions and the adsorption isotherm basically obeys the Flory–Huggins adsorption isotherm. Thermodynamic parameters for steel corrosion and inhibitor adsorption were determined, which revealed that the adsorption process is spontaneous.

Key words: Steel 4130, Ethylene glycol, Corrosion, Hydrodynamic, Nitrite

I. Danaee, M. Niknejad Khomami, A.A. Attar . Corrosion of AISI 4130 Steel Alloy under Hydrodynamic Condition in Ethylene Glycol+ Water+NO₂^-Solution[J]. J. Mater. Sci. Technol., 2013, 29(1): 89-96.

References

[1] L.Y. Xu, Y.F. Cheng, Corros. Sci. 50 (2008) 2094-3003.

[2] S. Tierce, N. Pébere, C. Blanc, C. Casenave, G. Mankowski,H. Robidou, Corros. Sci. 49 (2007) 4581-4590.

[3] S. Tierce, N. Pébere, C. Blanc, C. Casenave, G. Mankowski,H. Robidou, Electrochim. Acta 52 (2006) 1092-1097.

[4] O.K. Abiola, J.O.E. Otaigbe, Corros. Sci. 50 (2008) 242-249.

[5] G.A. Zhang, L.Y. Xu, Y.F. Cheng, Electrochim. Acta 53 (2008)8245-8252.

[6] A.M. Fekry, M.Z. Fatayerji, Electrochim. Acta 54 (2009) 6522.

[7] Y.S. Choi, J.J. Shim, J.G. Kim, J. Alloy Compd. 391 (2005)162-169.

[8] H. Fang, X. Hui, G. Chen, J. Alloy. Compd. 464 (2008) 292-295.

[9] E. Samiento-Bustos, J.G. González Rodriguez, J. Uruchurtu,G. Dominguez-Patiño, V.M. Salinas-Bravo, Corros. Sci. 50(2008) 2296-2303.

[10] E. Samiento-Bustos, J.G. González-Rodriguez, J. Uruchurtu,V.M. Salinas-Bravo, Corros. Sci. 51 (2009) 1107-1114.

[11] E. Blasco-Tamarit,A. Igual-Muñoz, J.GarcíaAntón,D.García-García,Corros. Sci. 48 (2006) 863-886.

[12] Y.C. Chen, C.M. Lee, S.K. Yen, S.D. Chyou, Corros. Sci. 49 (2007)3917-3925.

[13] A.M. Cabral, W. Trabelsi, R. Serra, M.F. Montemor, M.L.Zheludkevich, M.G.S. Ferreira, Corros. Sci. 48 (2006)3740-3758.

[14] S.S. Abd El Rehima, S.M. Sayyah, M.M. El-Deeb, S.M. Kamal,R.E. Azooz, Mater. Chem. Phys. 123 (2010) 20-27.

[15] A. Igual Muñoz, J. García Antón, S. López Nuévalos, J.L. Guiñón,V. Pérez Herranz, Corros. Sci. 46 (2004) 2955-2974.

[16] K.N. Mohana, A.M. Badiea, Corros. Sci. 50 (2008) 2939-2947.

[17] S.M. Abd El Haleem, S. Abd El Wanees, E.E. Abd El Aal, A. Diab,Corros. Sci. 52 (2010) 292-302.

[18] D. Wang, X. Tang, Y. Qiu, F. Gan, G.Z. Chen, Corros. Sci. 47(2005) 2157-2172.

[19] K. Aramaki, Corros. Sci. 43 (2001) 2201-2215.

[20] H. Wang, R. Akid, Corros. Sci. 50 (2008) 1142-1148.

[21] I. Danaee, S. Noori, Int. J. Hydrogen Energy 36 (2011) 12102-12111.

[22] J.R. Macdonald, Solid State Ionics 13 (1984) 147-149.

[23] I. Danaee, M. Jafarian, F. Forouzandeh, F. Gobal, M.G. Mahjani,J. Phys. Chem. B 112 (2008) 15933-15940.

[24] I. Danaee, J. Electroanal. Chem. 662 (2011) 415-420.

[25] G. Song, D. StJohn, Corros. Sci. 46 (2004) 1381-1399.

[26] M. Jafarian, F. Gobal, I. Danaee, R. Biabani, M.G. Mahjani,Electrochim. Acta 53 (2008) 4528-4536.

[27] M.B. Valcarce, M. Vázquez, Electrochim. Acta 53 (2008) 5007-5015.

[28] A.G. Muñoz, J.W. Schultze, Electrochim. Acta 49 (2004) 293-301.

[29] S.A.M. Refaey, S.S. Abd El-Rehim, F. Taha, M.B. Saleh, R.A.Ahmed, Appl. Surf. Sci. 158 (2000) 190-196.

[30] F. Bentiss, M. Lebrini, M. Lagrenée, Corros. Sci. 47 (2005) 2915-2931.

[31] M.S. Morad, A.M. Kamal El-Dean, Corros. Sci. 48 (2006) 3398-3412.

[32] L. Herrag, B. Hammouti, S. Elkadiri, A. Aouniti, C. Jama,H. Vezin, F. Bentiss, Corros. Sci. 52 (2010) 3042-3051.

[33] A.S. Fouda, A.A. Al-Sarawy, Desalination 201 (2006) 1-13.

[34] T. Szauer, A. Brandt, Electrochim. Acta 26 (1981) 1257-1260.

[35] R. Solmaz, G. Kardas, M. Culha, B. Yaz?c?, M. Erbil, Electrochim.Acta 53 (2008) 5941-5952.

[36] G.N. Mu, X.M. Li, F. Li, Mater. Chem. Phys. 86 (2004) 59-68.

[37] I. Ahamad, R. Prasad, M.A. Quraishi, Corros. Sci. 52 (2010)933-942.

[38] L.M. Vracar, D.M. Drazic, Corros. Sci. 44 (2002) 1669-1680.

[39] S.E. Nataraja, T.V. Venkatesha, K. Manjunatha, B. Poojary,M.K. Pavithra, H.C. Tandon, Corros. Sci. 53 (2011) 2651-2659.

[40] X. Li, G. Mu, Appl. Surf. Sci. 252 (2005) 1254-1265.

[41] J.M. Bastidas, P. Pinilla, E. Cano, J.L. Polo, S. Miguel, Corros. Sci.45 (2003) 427-449.

[42] M. Bouklah, B. Hammouti, M. Lagrenee, F. Bentiss, Corros. Sci.48 (2006) 2831-2842.

[43] M. Bouklah, N. Benchat, B. Hammouti, A. Aouniti, S. Kertit,Mater. Lett. 60 (2006) 1901-1905.

[44] G. Mu, X. Li, G. Liu, Corros. Sci. 47 (2005) 1932-1952.

[45] N.P. Cosman, K. Fatih, S.G. Roscoe, J. Electroanal. Chem. 574(2005) 261-271.

[46] S. Tamil Sevil, V. Raman, N. Rajendran, J. Appl. Electrochem. 33(2003) 1175-1182.

[47] M. Outirite, M. Lagrenee, M. Lebrini, M. Traisnel, C. Jama,H. Vezin, F. Bentiss, Electrochim. Acta 55 (2010) 1670-1681.

Corrosion of AISI 4130 Steel Alloy under Hydrodynamic Condition in Ethylene Glycol+ Water+NO₂^-Solution

RichHTML

Knowledge

Abstract

Cite this article

share this article

References

Related Articles 15

Recommended Articles

Metrics

Comments

[1]	Yanxin Qiao, Daokui Xu, Shuo Wang, Yingjie Ma, Jian Chen, Yuxin Wang, Huiling Zhou. Effect of hydrogen charging on microstructural evolution and corrosion behavior of Ti-4Al-2V-1Mo-1Fe alloy [J]. J. Mater. Sci. Technol., 2021, 60(0): 168-176.
[2]	Jiawei Ding, Haitao Wang, En-Hou Han. A multiphysics model for studying transient crevice corrosion of stainless steel [J]. J. Mater. Sci. Technol., 2021, 60(0): 186-196.
[3]	Hongxia Wan, Dongdong Song, Xiaolei Shi, Yong Cai, Tingting Li, Changfeng Chen. Corrosion behavior of Al_0.4CoCu_0.6NiSi_0.2Ti_0.25 high-entropy alloy coating via 3D printing laser cladding in a sulphur environment [J]. J. Mater. Sci. Technol., 2021, 60(0): 197-205.
[4]	Hu Liu, Jie Wei, Junhua Dong, Yiqing Chen, Yumin Wu, Yangtao Zhou, Subedi Dhruba Babu, Wei Ke. Influence of cementite spheroidization on relieving the micro-galvanic effect of ferrite-pearlite steel in acidic chloride environment [J]. J. Mater. Sci. Technol., 2021, 61(0): 234-246.
[5]	Yanhua Zeng, Fenfen Yang, Zongning Chen, Enyu Guo, Minqiang Gao, Xuejian Wang, Huijun Kang, Tongmin Wang. Enhancing mechanical properties and corrosion resistance of nickel-aluminum bronze via hot rolling process [J]. J. Mater. Sci. Technol., 2021, 61(0): 186-196.
[6]	Xian-Zong Wang, Hong-Qiang Fan, Triratna Muneshwar, Ken Cadien, Jing-Li Luo. Balancing the corrosion resistance and through-plane electrical conductivity of Cr coating via oxygen plasma treatment [J]. J. Mater. Sci. Technol., 2021, 61(0): 75-84.
[7]	C.Q. Li, D.K. Xu, Z.R. Zhang, E.H. Han. Influence of the lithium content on the negative difference effect of Mg-Li alloys [J]. J. Mater. Sci. Technol., 2020, 57(0): 138-145.
[8]	Di Zhang, Zhen Zhang, Yanlin Pan, Yanbin Jiang, Linzhong Zhuang, Jishan Zhang, Xinfang Zhang. Current-driving intergranular corrosion performance regeneration below the precipitates solvus temperature in Al-Mg alloy [J]. J. Mater. Sci. Technol., 2020, 53(0): 132-139.
[9]	Han Yan, Meng Cai, Wen Li, Xiaoqiang Fan, Minhao Zhu. Amino-functionalized Ti₃C₂T_x with anti-corrosive/wear function for waterborne epoxy coating [J]. J. Mater. Sci. Technol., 2020, 54(0): 144-159.
[10]	Enze Zhou, Jianjun Wang, Masoumeh Moradi, Huabing Li, Dake Xu, Yuntian Lou, Jinheng Luo, Lifeng Li, Yulei Wang, Zhenguo Yang, Fuhui Wang, Jessica A. Smith. Methanogenic archaea and sulfate reducing bacteria induce severe corrosion of steel pipelines after hydrostatic testing [J]. J. Mater. Sci. Technol., 2020, 48(0): 72-83.
[11]	Zhuowei Tan, Liuyang Yang, Dalei Zhang, Zhenbo Wang, Frank Cheng, Mingyang Zhang, Youhai Jin. Development mechanism of internal local corrosion of X80 pipeline steel [J]. J. Mater. Sci. Technol., 2020, 49(0): 186-201.
[12]	Jiajun Luo, Maryam Tamaddon, Changyou Yan, Shuanhong Ma, Xiaolong Wang, Feng Zhou, Chaozong Liu. Improving the fretting biocorrosion of Ti₆Al₄V alloy bone screw by decorating structure optimised TiO₂ nanotubes layer [J]. J. Mater. Sci. Technol., 2020, 49(0): 47-55.
[13]	Zhao-Qi Zhang, Rong-Chang Zeng, Cun-Guo Lin, Li Wang, Xiao-Bo Chen, Dong-Chu Chen. Corrosion resistance of self-cleaning silane/polypropylene composite coatings on magnesium alloy AZ31 [J]. J. Mater. Sci. Technol., 2020, 41(0): 43-55.
[14]	Wei Xu, Xin Lu, Jingjing Tian, Chao Huang, Miao Chen, Yu Yan, Luning Wang, Xuanhui Qu, Cuie Wen. Microstructure, wear resistance, and corrosion performance of Ti35Zr28Nb alloy fabricated by powder metallurgy for orthopedic applications [J]. J. Mater. Sci. Technol., 2020, 41(0): 191-198.
[15]	Hui Pan, Liwei Wang, Yi Lin, Feng Ge, Kang Zhao, Xin Wang, Zhongyu Cui. Mechanistic study of ammonium-induced corrosion of AZ31 magnesium alloy in sulfate solution [J]. J. Mater. Sci. Technol., 2020, 54(0): 1-13.