Effect of Si3N4 Addition on the Mechanical Properties, Microstruc-tures, and Wear Resistance of Ti-6Al-4V Alloy

Abstract

Abstract: In order to improve the wear resistance of Ti-6Al-4V, different amounts of Si3N4 powder were added into the alloy powder and sintered at 1250℃. Porous titanium alloy with higher wear resistance was successfully fabricated. At sintering temperature, reaction took place and a new hard phase of Ti5Si3 formed. The mechanical properties of the fabricated alloys with different amounts of Si3N4 addition were investigated. The hardness of Ti-6Al-4V, which is the index of wear resistance, was increased by the addition of Si3N4. Amounts of Si3N4 addition have very significant influences on hardness and compressive strength. In present study, titanium alloy with 5 wt pct Si3N4 addition has 62% microhardness and 45% overall bulk hardness increase, respectively. In contrast, it has a 16.4% strength reduction. Wear resistance was evaluated by the weight loss during wear test. A new phase of Ti5Si3 was detected by electron probe microanalyzer (EPMA) and X-ray diffraction (XRD) method. The original Si3N4 decomposed during sintering and transformed into titanium silicide. Porous structure was achieved due to the sintering reaction.

Key words: Ti-6Al-4V, Silicon nitride, Sintering reaction, Mechanical properties

Ruihua HU, Montasser M.Dewidar, Hyo-Jin KIM, Jae-Kyoo LIM. Effect of Si3N4 Addition on the Mechanical Properties, Microstruc-tures, and Wear Resistance of Ti-6Al-4V Alloy[J]. J Mater Sci Technol, 2007, 23(02): 257-261.

References

[1] M．Long and H．J．Rack:Biomaterials,1998,19,1621．
[2] T．Kokubo,H．M．Kim,M．Kawashita and T．Nakamura: J．Mater．Sci．-Mater．M．,2004,15(2),99．
[3] D．Paul,P．D．Bianco and M．C．John: Biomaterials, 1996,17,1937．
[4]M．M．Dewidar,H．C．Yoon and J．K．Lim:Met．Mater．- Int．,2006,12(3),193．
[5]Z．Cai,H．Nakajima, M．Woldu, A．Berglund, M．Bergman and T．Okabe:Biomaterials,1999,20, 183．
[6] M．A．Khan,R．L．Williams and D．F．Williams:Bioma- terials,1996,17,2117．
[7] M．Koike and H．Fuji:Biomaterials,2001,22,2931．
[8] H．Choe,S．M．Abkowitz and S．Abkowitz:Mater．Sci．Eng．A,2005,396,99．
[9] M．Niinomi:Mater．Sci．Eng．A,1998,243,231．
[10]K．Mishra, J．A．Davidson, R．A．Poggi,P．Kovacs, T．J．Fitzgerald and J．E．Lemons: ASTM sTP, Vol．1272,ASTM,West Conshohocken,PA,1996,96．
[11]M．S．Selamat,L．M．Watson and T．N．Baker:J．Mater．Process．Technol．,2003,14,2725．
[12] E．Zeiler,D．Klaffke,K．Hiltner and T．Grogler:Surf. Coat．Technol．,1999,116,599．
[13] E．Yun,K．Lee and S．Lee:Surf．Coat．Teehnol．,2005, 191,83．
[14] Z．P．Yao,Z．H．Jiang,X．T．Sun,S．G．Xin and Z．D．Wu: Mater．Chem．Phys．,2005,92,408．
[15] ASTM Standards,E9-89a,ASTM Int．,West Con- shohocken,2000,PA19428-2959．
[16] ASTM Standards,E384-99el,ASTM Int．,West Con- shohocken,2000,PA19428-2959．
[17] J．Zeltinger,J．K．Sherwood,D．A．Graham,R．Mueller and L．G．Griffith:Tissue Eng．,2001,7,557．
[18] I．Zein,D．W．Hutmacher,K．C．Tan and S．H．Tecoh: Biomaterials,2002,23,1169．
[19] D．W．Hutmacher,T．Schantz, I．Zein, K．W．Ng, S.H.Teoh and K．C．Tan:J．Biomed．Mater．Res．, 2001,55,203．
[20]Rongjiu LI:Ceramic-Metal Composites, Metallurgy Industry Press,Beijing,2004,194．(in Chinese)
[21] A．J．Thom and M．K．Meyer:Processing and Fabrica- tion of Advanced Materials　III, TMS,Warrendale, USA,1994．