J. Mater. Sci. Technol. ›› 2015, Vol. 31 ›› Issue (11): 1144-1150.DOI: 10.1016/j.jmst.2015.09.002
• Orginal Article • Previous Articles Next Articles
H.C. Wu1, B. Yang1, 2, Y.Z. Shi1, Q. Gao1, Y.Q. Wang3
Received:
2015-01-05
Contact:
* Corresponding author. Ph.D.; Tel.: +86 1062333351; Fax: +86 10 62333351.E-mail address: Supported by:
H.C. Wu, B. Yang, Y.Z. Shi, Q. Gao, Y.Q. Wang. Crack Initiation Mechanism of Z3CN20.09M Duplex Stainless Steel during Corrosion Fatigue in Water and Air at 290?°C[J]. J. Mater. Sci. Technol., 2015, 31(11): 1144-1150.
[1] L. Llanes, A. Mateo, P. Villechaise, J. Méndez, M. Anglada,Int. J. Fatigue, 21 (1999), pp. S119-S125 [2] Y.Q. Wang, J. Han, H.C. Wu, B. Yang, X.T. Wang,Nucl. Eng. Des, 259 (2013), p. 1 [3] J.K. Sahu, U. Krupp, H.J. Christ,Int. J. Fatigue, 45 (2012), pp. 8-14 [4] Y.Q. Wang, B. Yang, J. Han, H.C. Wu, X.T. Wang,Mater. Trans, 54 (2013), pp. 839-843 [5] O.H.I.I. Khalifa,J. Mater. Sci. Technol, 26 (2010), pp. 810-816 [6] A.M.K. Dehghani,J. Mater. Sci. Technol, 26 (2010), pp. 851-857 [7] A. Mateo, A. Gironès, J. Keichel, L. Llanes, N. Akdut, M. Anglada,Mater. Sci. Eng. A, 314 (2001), pp. 176-185 [8] A. Gironès, P. Villechaise, A. Mateo, M. Anglada, J. Méndez,Mater. Sci. Eng. A, 387-389 (2004), pp. 516-521 [9] S. Xu, X.Q. Wu, E.H. Han, W. Ke, Y. Katada,Mater. Sci. Eng. A, 490 (2008), pp. 16-25 [10] F. Xue, Z. Wang, G. Shu, W. Yu, H. Shi, W. Ti,Nucl. Eng. Des, 239 (2009), pp. 2217-2223 [11] X.Q. Wu, Y. Katada,Mater. Sci. Eng. A, 379 (2004), pp. 58-71 [12] R. Ebara,Procedia Eng, 2 (2010), pp. 1297-1306 [13] H.P. Seifert, S. Ritter, H.J. Leber,Corros. Sci, 55 (2012), pp. 61-75 [14] S. Ritter, H.P. Seifert,J. Nucl. Mater, 375 (2008), pp. 72-79 [15] K.M. Perkins, M.R. Bache,Int. J. Fatigue, 27 (2005), pp. 1499-1508 [16] W. Zhao, Y. Wang, T. Zhang, Y. Wang,Corros. Sci, 57 (2012), pp. 99-103 [17] M.D. Roach, S.I. Wright, J.E. Lemons, L.D. Zardiackas,Mater. Sci. Eng. A, 586 (2013), pp. 382-391 [18] P. Mu, V. Aubin, I. Alvarez-Armas, A. Armas,Mater. Sci. Eng. A, 573 (2013), pp. 45-53 [19] M. Balbi, M. Avalos, A. El Bartali, I. Alvarez-Armas,Int. J. Fatigue, 31 (2009), pp. 2006-2013 [20] D.J. Morrison, J.C. Moosbrugger,Int. J. Fatigue, 19 (1997), pp. 51-59 [21] J.V. Carstensen, T. Magnin,Int. J. Fatigue, 23 (2001), pp. 195-200 [22] V.S. Srinivasan, R. Sandhya, M. Valsan, K. Bhanu Sankara Rao, S.L. Mannan,Int. J. Fatigue, 26 (2004), pp. 1295-1302 [23] M. Ramesh, H.J. Leber, M. Diener, R. Spolenak,J. Nucl. Mater, 415 (2011), pp. 23-30 [24] D.W. Kim, W. Ryu, J.H. Hong, S. Choi,J. Nucl. Mater, 254 (1998), pp. 226-233 [25] M.C. Marinelli, S. Degallaix, I. Alvarez-Armas,Mater. Sci. Eng. A, 435-436 (2006), pp. 305-308 [26] S.M. Yin, S.X. Li,J. Mater. Sci. Technol, 29 (2013), pp. 775-780 [27] T. Magnin, C. Ramade, J. Lepinoux, L.P. Kubin,Mater. Sci. Eng. A, 118 (1989), pp. 41-51 [28] R. Strubbia, S. Hereñú, A. Giertler, I. Alvarez-Armas, U. Krupp,Int. J. Fatigue, 65 (2014), pp. 58-63 [29] I. Alvarez-Armas, H. Knobbe, M.C. Marinelli, M. Balbi, S. Hereñú, U. Krupp,Procedia Eng, 10 (2011), pp. 1491-1496 [30] J. Man, T. Vystavěl, A. Weidner, I. Kuběna, M. Petrenec, T. Kruml, J. Polák,Int. J. Fatigue, 39 (2012), pp. 44-53 [31] B. Deng, Z. Wang, Y. Jiang, H. Wang, J. Gao, J. Li,Electrochim. Acta, 54 (2009), pp. 2790-2794 [32] A. Pardo, M.C. Merino, A.E. Coy, F. Viejo, R. Arrabal, E. Matykina,Corros. Sci, 50 (2008), pp. 1796-1806 [33] C.A. Olsson,Corros. Sci, 37 (1995), pp. 467-479 [34] H.C. Wu, B. Yang, S.L. Wang, M.X. Zhang,Mater. Sci. Eng. A, 633 (2015), pp. 176-183 |
[1] | Zhihong Wu, Hongchao Kou, Nana Chen, Mengqi Zhang, Ke Hua, Jiangkun Fan, Bin Tang, Jinshan Li. Duality of the fatigue behavior and failure mechanism in notched specimens of Ti-7Mo-3Nb-3Cr-3Al alloy [J]. J. Mater. Sci. Technol., 2020, 50(0): 204-214. |
[2] | Xingchen Xu, Daoxin Liu, Xiaohua Zhang, Chengsong Liu, Dan Liu. Mechanical and corrosion fatigue behaviors of gradient structured 7B50-T7751 aluminum alloy processed via ultrasonic surface rolling [J]. J. Mater. Sci. Technol., 2020, 40(0): 88-98. |
[3] | H.F. Li, Z.Z. Shi, L.N. Wang. Opportunities and challenges of biodegradable Zn-based alloys [J]. J. Mater. Sci. Technol., 2020, 46(0): 136-138. |
[4] | Pingli Jiang, Carsten Blawert, Jan Bohlen, Mikhail L. Zheludkevich. Corrosion performance, corrosion fatigue behavior and mechanical integrity of an extruded Mg4Zn0.2Sn alloy [J]. J. Mater. Sci. Technol., 2020, 59(0): 107-116. |
[5] | Jun Gao, Jibo Tan, Ming Jiao, Xinqiang Wu, Lichen Tang, Yifeng Huang. Role of welding residual strain and ductility dip cracking on corrosion fatigue behavior of Alloy 52/52M dissimilar metal weld in borated and lithiated high-temperature water [J]. J. Mater. Sci. Technol., 2020, 42(0): 163-174. |
[6] | Xumin Zhu, Congyang Gong, Yun-Fei Jia, Runzi Wang, Chengcheng Zhang, Yao Fu, Shan-Tung Tu, Xian-Cheng Zhang. Influence of grain size on the small fatigue crack initiation and propagation behaviors of a nickel-based superalloy at 650 °C [J]. J. Mater. Sci. Technol., 2019, 35(8): 1607-1617. |
[7] | Dan Liu, Ru Jia, Dake Xu, Hongying Yang, Ying Zhao, M. saleem Khan, Songtao Huang, Jiankang Wen, Ke Yang, Tingyue Gu. Biofilm inhibition and corrosion resistance of 2205-Cu duplex stainless steel against acid producing bacterium Acetobacter aceti [J]. J. Mater. Sci. Technol., 2019, 35(11): 2494-2502. |
[8] | Lijin Dong, Qunjia Peng, En-Hou Han, Wei Ke, Lei Wang. Microstructure and intergranular stress corrosion cracking susceptibility of a SA508-52M-316L dissimilar metal weld joint in primary water [J]. J. Mater. Sci. Technol., 2018, 34(8): 1281-1292. |
[9] | Ying Wu, Jianrong Liu, Hao Wang, Shaoxuan Guan, Rui Yang, Hongfu Xiang. Effect of stress ratio on very high cycle fatigue properties of Ti-10V-2Fe-3Al alloy with duplex microstructure [J]. J. Mater. Sci. Technol., 2018, 34(7): 1189-1195. |
[10] | Jun Li, Yixun Yang, Yibin Ren, Jiahui Dong, Ke Yang. Effect of cold deformation on corrosion fatigue behavior of nickel-free high nitrogen austenitic stainless steel for coronary stent application [J]. J. Mater. Sci. Technol., 2018, 34(4): 660-665. |
[11] | Xuequn Cheng, Yi Wang, Xiaogang Li, Chaofang Dong. Interaction between austein-ferrite phases on passive performance of 2205 duplex stainless steel [J]. J. Mater. Sci. Technol., 2018, 34(11): 2140-2148. |
[12] | Ming Wang, Ting Xu, Yanli Zhu, Wenhong Yin, Hong Guo, Ertuan Zhao, Xiaoying Fang, Weiguo Wang. Evolution of interface character distribution in duplex stainless steel processed by cross-rolling and annealing [J]. J. Mater. Sci. Technol., 2018, 34(11): 2160-2166. |
[13] | Cheng Ma, Qunjia Peng, Jinna Mei, En-Hou Han, Wei Ke. Microstructure and corrosion behavior of the heat affected zone of a stainless steel 308L-316L weld joint [J]. J. Mater. Sci. Technol., 2018, 34(10): 1823-1834. |
[14] | Wen Wang, Ruiqi Xu, Yaxin Hao, Qiang Wang, Liangliang Yu, Qianying Che, Jun Cai, Kuaishe Wang, Zongyi Ma. Corrosion fatigue behavior of friction stir processed interstitial free steel [J]. J. Mater. Sci. Technol., 2018, 34(1): 148-156. |
[15] | Li Ping, Zhao Yang, Liu Yuzhi, Zhao Ying, Xu Dake, Yang Chunguang, Zhang Tao, Gu Tingyue, Yang Ke. Effect of Cu Addition to 2205 Duplex Stainless Steel on the Resistance against Pitting Corrosion by the Pseudomonas aeruginosa Biofilm [J]. J. Mater. Sci. Technol., 2017, 33(7): 723-733. |
Viewed | ||||||
Full text |
|
|||||
Abstract |
|
|||||