Cavitation Erosion Corrosion Behaviour of Manganese-nickel-aluminum Bronze in Comparison with Manganese-brass

Abstract

Abstract:

The cavitation erosion corrosion behaviour of ZQMn12-8-3-2 manganese-nickel-aluminum bronze and ZHMn55-3-1 manganese-brass was investigated by mass loss, electrochemical measurements (polarization curves and electrochemical impedance spectroscopy) and the cavitation damaged surfaces were observed by scanning electron microscopy (SEM). The results showed that ZQMn12-8-3-2 had better cavitation erosion resistance than ZHMn55-3-1. After the cavitation erosion for 6 h, the cumulative mass loss of ZQMn12-8-3-2 was about 1/3 that of ZHMn55-3-1. The corrosion current density of ZQMn12-8-3-2 was less than that of ZHMn55-3-1 under both static and cavitaiton condition. The free-corrosion potentials of ZQMn12-8-3-2 and ZHMn55-3-1 were all shifted in positive direction under cavitation condition compared to static condition. In the total cu-mulative mass loss under cavitation condition, the pure erosion played a key role for the two tested materials (74% for ZHMn55-3-1 and 60% for ZQMn12-8-3-2), and the total synergism between corrosion and erosion of ZQMn12-8-3-2 (39%) was larger than that of ZHMn55-3-1 (23%). The high cavitation erosion resistance of ZQMn12-8-3-2 was mainly attributed to its lower stacking fault energy (SFE), the higher microhardness and work-hardening ability as well as the favorable propagation of cavitation cracks for ZQMn12-8-3-2, i.e., parallel to the surface rather than perpendicular to the surface for ZHMn55-3-1.

Key words: Cavitation erosion, Marine propeller, Manganese-nickel-aluminum bronze, Manganese-brass, Synergism, Work-hardening ability, Stacking fault energy

Hong Yu,Yugui Zheng,Zhiming Yao. Cavitation Erosion Corrosion Behaviour of Manganese-nickel-aluminum Bronze in Comparison with Manganese-brass[J]. J Mater Sci Technol, 2009, 25(06): 758-766.

References

[1 ] A. Karimi and J.L. Martin: Int. Metal Rev., 1986, 31, 1.
[2 ] S.Z. Luo, Y.G. Zheng, M.C. Li, Z.M. Yao and W. Ke: Corrosion, 2003, 59, 597.
[3 ] C.H. Tang, F.T. Cheng and H.C. Man: Surf. Coat. Technol., 2006, 200, 2594.
[4 ] R.J.K. Wood and S.A. Fry: J. Fluids Eng., 1989, 111, 271.
[5 ] A. Al-Hashem and W. Riad: Mater. Charact., 2002, 48, 37.
[6 ] A. Al-Hashem, P.G. Caceres, W.T. Riad and H.M. Shalaby: Corrosion, 1995, 51, 331.
[7 ] X.F. Zhang and L. Fang: Wear, 2002, 253, 1105.
[8 ] R.C. Barik, J.A. Wharton, R.J.K. Wood, K.S. Tan and K.R. Stokes: Wear, 2005, 259, 230.
[9 ] C.H. Tang, F.T. Cheng and H.C. Man: Surf. Coat. Technol., 2006, 200, 2602.
[10] C.H. Tang, F.T. Cheng and H.C. Man: Mater. Sci. Eng. A, 2004, 373, 195.
[11] X.Y. Li, Y.G. Yan, L. Ma, Z.M. Xu and J.G. Li: Mater. Sci. Eng. A, 2004, 382, 82.
[12] A.V. Reddy, G. Sundararajan, R. Sivakumar and P. R.Rao: Acta Metall., 1984, 32, 1305.
[13] N.P. Suh and N. Saka: Wear, 1977, 44, 135.
[14] ASTM G32-85: Standard Method of Vibratory Cavition Erosion Test, West Conshohocken, ASTM International, PA, 1985, 187.
[15] C.M. Preece: Cavitation Erosion. Treatise on Material Science and Technology, Academic Press, New York, 1979, 249.
[16] C.N. Cao: Corrosion Electrochemistry, Chemistry Industry Press, Bejing, 2004, 213. (in Chinese)
[17] A. Neville, T. Hodgkiess and J. T.Dallas: Wear, 1995, 186/187, 497.
[18] Y.G. Zheng, Z.M. Yao, X.Y. Wei and W. Ke: Wear, 1995, 186/187, 555.
[19] K.R. Trethewey, T.J. Haley and C.C. Clark: Brit. Corros. J., 1988, 23, 55.
[20] R.J.K. Wood and S.P. Hutton: Wear, 1990, 140, 387.
[21] B.C. Syrett: Corrosion, 1976, 32, 242.
[22] P. Brezina: Int. Metal Rev., 1982, 27, 77.
[23] J.L. Gonalez, R. Aranda and M. Jonapa: Proc. Conf. on Application of Stainless Steel092, Vol. 2, Stockholm, Sweden, 1992, 1009.
[24] W. Liu, Y.G. Zheng, C.S. Liu, Z.M. Yao and W. Ke: Wear, 2003, 254, 713.

[1]	Zhengliang Liu, Shenglong Zhu, Mingli Shen, Yixuan Jia, Wen Wang, Fuhui Wang. Microstructure and cavitation erosion behavior of sputtered NiCrAlTi coatings with and without N incorporations [J]. J. Mater. Sci. Technol., 2020, 54(0): 211-222.
[2]	Seok Gyu Lee, Bohee Kim, Min Cheol Jo, Kyeong-Min Kim, Junghoon Lee, Jinho Bae, Byeong-Joo Lee, Seok Su Sohn, Sunghak Lee. Effects of Cr addition on Charpy impact energy in austenitic 0.45C-24Mn-(0,3,6)Cr steels [J]. J. Mater. Sci. Technol., 2020, 50(0): 21-30.
[3]	Enkang Hao, Yulong An, Xia Liu, Yijing Wang, Huidi Zhou, Fengyuan Yan. Effect of annealing treatment on microstructures, mechanical properties and cavitation erosion performance of high velocity oxy-fuel sprayed NiCoCrAlYTa coating [J]. J. Mater. Sci. Technol., 2020, 53(0): 19-31.
[4]	T. Cai, K.Q. Li, Z.J. Zhang, P. Zhang, R. Liu, J.B. Yang, Z.F. Zhang. Predicting the variation of stacking fault energy for binary Cu alloys by first-principles calculations [J]. J. Mater. Sci. Technol., 2020, 53(0): 61-65.
[5]	K.Q. Li, Z.J. Zhang, J.X. Yan, J.B. Yang, Z.F. Zhang. Mechanism transition of cross slip with stress and temperature in face-centered cubic metals [J]. J. Mater. Sci. Technol., 2020, 57(0): 159-171.
[6]	Xinglong An, Hao Zhang, Song Ni, Xiaoqin Ou, Xiaozhou Liao, Min Song. Effects of temperature and alloying content on the phase transformation and {10$\bar{1}$1} twinning in Zr during rolling [J]. J. Mater. Sci. Technol., 2020, 41(0): 76-80.
[7]	H.F. Zhang, H.L. Yan, H. Yu, Z.W. Ji, Q.M. Hu, N. Jia. The effect of Co and Cr substitutions for Ni on mechanical properties and plastic deformation mechanism of FeMnCoCrNi high entropy alloys [J]. J. Mater. Sci. Technol., 2020, 48(0): 146-155.
[8]	Zhang Zhefeng, Li Linlin, Zhang Zhenjun, Zhang Peng. Twin boundary: Controllable interface to fatigue cracking. [J]. J. Mater. Sci. Technol., 2017, 33(7): 603-606.
[9]	Chen Xiaoguang, Xie Ruishan, Lai Zhiwei, Liu Lei, Yan Jiuchun, Zou Guisheng. Interfacial Structure and Formation Mechanism of Ultrasonic-assisted Brazed Joint of SiC Ceramics with Al-12Si Filler Metals in Air [J]. J. Mater. Sci. Technol., 2017, 33(5): 492-498.
[10]	Tian Sugui,Zhu Xinjie,Wu Jing,Yu Huichen,Shu Delong,Qian Benjiang. Influence of Temperature on Stacking Fault Energy and Creep Mechanism of a Single Crystal Nickel-based Superalloy [J]. J. Mater. Sci. Technol., 2016, 32(8): 790-798.
[11]	S. Srinivasa Rao, B.V. Appa Rao, S. Roopas Kiran, B. Sreedhar. Lactobionic Acid as a New Synergist in Combination with Phosphonate–Zn(II) System for Corrosion Inhibition of Carbon Steel [J]. J. Mater. Sci. Technol., 2014, 30(1): 77-89.
[12]	Xiaoya, Yonggui YAN, Zhenming XU, Jianguo LI. Cavitation Erosion Behavior of as-Welded Cu12Mn8Al3Fe2Ni Alloy [J]. J Mater Sci Technol, 2004, 20(03): 304-306.
[13]	Suzhen LUO, Yugui ZHENG, Wei LIU, Heming JING, Zhiming YAO, Wei KE. Cavitation Erosion Behavior of CrMnN Duplex Stainless Steel in Distilled Water and 3% NaCl Solution [J]. J Mater Sci Technol, 2003, 19(04): 346-350.
[14]	YANG Zhi'an SHI Changxu XIAO Yaotian Institute of Metal Research,Academia Sinica,Shenyang,110015,China.. Variation in Creep Rupture of γ′ Strengthened Superalloys with Stacking Fault Energy of Matrices [J]. J Mater Sci Technol, 1990, 6(4): 250-256.