Abstract: A cost effective method was introduced to fabricate pure aluminum matrix composites reinforced with 20% volume fraction of 3.5 μm SiC particles by squeeze casting followed by hot extrusion. In order to lower volume fraction of the composites, a mixed preform containing pure aluminum powder and the SiC particles was used. The suitable processing parameters for the infiltration of pure aluminum melt into the mixed preform are: melt temperature 800℃, preform temperature 500℃, infiltration pressure 5 MPa, and solidification pressure 50 MPa. Microstructure and properties of the composites in both as-cast and hot extruded states were investigated. The results indicate that hot extrusion can obviously improve the mechanical properties of the composite.

Key words: Aluminum, Particulate reinforced composites, Casting, Liquid infiltration