Abstract: Microstructure and mechanical properties of hyper-eutectic Al-Si alloy fabricated by spray casting were investigated and then these results were compared with those by squeeze cast. The spray-cast specimen was found to have finer Si particles (～5 μm) compared to the squeeze-cast specimen (10–25 μm). The tensile strength and elongation of the spray-cast specimen are also higher than those of the squeeze cast one. It was considered that the increased mechanical properties of the spray-cast specimen were mainly due to finer size of the Si particles distributed in Al matrix.

Key words: Hyper-eutectic Al-Si alloy, Squeeze casting, Spray casting