A Partial 1100℃ Isotherm of Ti-Ni-Si Ternary System

Xiaohua HU; Yimin LIU; Guoliang CHEN and Kequan NI (State Key Lab. for Adv. Met. Mater., University of Science & Technology Beijing, Beijing 100083, China)   

  • Received:1998-03-28 Revised:1998-03-28 Online:1998-03-28 Published:2009-10-10

Abstract: A partial section of Ti-Ni-Si ternary system at 1100℃was constituted with Ni less than 50 at.pct. Twelve single phase areas were determined. The binary Ti3Si phase proposed to occur at 1100℃ was not found in our investigations. A phase with the composition of Ni2Ti9Si9 detected is possibly a new phase. No linear ternary compound was found. Some of these compounds show noticeable composition range