Abstract: Growth of In0.52Al0.48As epilayers on InP (100) substrates by molecular beam epitaxy at a wide range of substrate tempreatures (470~550℃) and at different Si doping levels has been carried out. Low temperature photoluminescence (PL) and double-axis X-ray diffraction (XRD) analyses shaw a strong dependence of the PL and XRD linewidths, XRD intensity ratio (Lepi/Isub), and lattice-mismatch on the substrate temperature. The X-ray diffraction peaks of samples grown at law temperatures show a composition of smaller peaks, indicating the presence of disorder due to alloy clustering. Raman scattering measurements of the same samples show an additional higher energy mode at 273 cm-1 in addition to the InAs-like and AlAs-like longitudinal-optic (LO) phonon modes. Samples doped with Si show an inverted S-shaped dependence of the PL peak energy variation with the temperature which weakens at high doping levels due to a possible reduction in the donor binding energy. Supported be observations of a reduction in both the AlAs-like and InAs-like LO phonon frequencies and a broadening of the LO phonon line shape as the doping level is increased, the PL intensity also shows in increasing degrees at higher doping levels, a temperature dependence which is characteristic of disordered and amorphous materials.