J Mater Sci Technol ›› 1997, Vol. 13 ›› Issue (2): 145-148.
• Articles • Previous Articles Next Articles
Hongchao LIU ; Changlin KUO (Shanghai Institute of Ceramics, Chinese Academy of Sciences, Shanghai 200050, China)
Received:
Revised:
Online:
Published:
Abstract: In cooperation with figure-of-merits the Rietveld analysis can appraise both angular and intensity data of powder diffraction. In this work, X-ray diffraction pattern of Bi4(SiO4)3 was redetermined with intensity figure-of-merits, which qualify agreement between observed and calculated relative intensities. F30 is 158.90 (0.0059, 32), intensity figure of merit Rint is 8.7, I20(17), 8.0. The values of figure-of-merits show that the data of JCPDS cards are distorted. Both the experimental and calculated peak positions and heights are listed in detail.
Hongchao LIU ; Changlin KUO (Shanghai Institute of Ceramics, Chinese Academy of Sciences, Shanghai 200050, China). X-ray Powder Diffraction Pattern of Bi_4(SiO_4)_3[J]. J Mater Sci Technol, 1997, 13(2): 145-148.
0 / / Recommend
Add to citation manager EndNote|Ris|BibTeX
URL: https://www.jmst.org/EN/
https://www.jmst.org/EN/Y1997/V13/I2/145
WeChat