Structure and Anomalous Magnetic Properties in Fe-N/Ti-N Nano-multilayers

Zhenjun WANG; Xiangrong CHANG; Yousong GU ;Zhongzhuo TIAN and Jimei XIAO (Uuiversity of Science and Technology Beijing, Beijing 100083, China)Lishi WEN (Institute of Metal Research, Chinese Academy of Sciences, Shenyang 110015, China)(To whom corresponden   

  • Received:1996-03-28 Revised:1996-03-28 Online:1996-03-28 Published:2009-10-10

RichHTML

0

PDF (PC)

434

Abstract: DC-magnetron sputtering was employed to prepare Fe-N/Ti-N periodic nano-multilayers . Magnetic properties were studied by vibrating sample magnetometry and structure by TEM and X-ray diffraction for the films. A strong enhancement of the saturation magnetization was found in multilayers containing thinner Fe-N layers. The coercivity was found to be nearly constant. A kind of anomalous hysteresis loops was found in some samples

About JMST
  • About JMST
  • Editorial board
  • Coverage
  • Index in
    • Authors and reviewers
  • How to submit
  • Art instruction
  • Submission online
  • Instruction for reviewer
  • Reviewer login
  • Office login
    • Contact
  • Tel: +86-024-83978208
    E-mail: jmst@imr.ac.cn
    Address: 72 Wenhua Road, Shenyang, Liaoning, 110016, China
    • WeChat
    • Copyright © Editorial Office of Journal of Materials Sciences and Technology, All Rights Reserved.