J Mater Sci Technol ›› 1996, Vol. 12 ›› Issue (2): 119-123.

• Articles • Previous Articles     Next Articles

Phase Relationship in (Dy_(0.65)Tb_(0.25)Pr_(0.1))Fe_x Alloys (1.6≤x≤2.1)

Bowen WANG;Changheng WU ; Yuzhi CHUANG and Ximei JIN (Institute of Metal Research, Chinese Academy of Sciences, Shenyang 110015, China)(To whom correspondence should be addressed)(Present address: Shenyang Institute of Technology Shenyang, 110015, China)   

  • Received:1996-03-28 Revised:1996-03-28 Online:1996-03-28 Published:2009-10-10

RichHTML

0

PDF (PC)

358

Abstract: The microstructure and phase relationship of (Dy0.65Tb0.25Pr0.1)Fex alloys in the composition range of 1.6≤x≤2.1 were investigated using optical microscopy, X-ray diffraction , DTA and EPMA techniques. The variations of microstructure and lattice parameter with the iron content,the effect of heat treatment on the microstructure and the phase relationship have been studied.The phase relationship in the vicinity of the Laves phase is proposed

About JMST
  • About JMST
  • Editorial board
  • Coverage
  • Index in
    • Authors and reviewers
  • How to submit
  • Art instruction
  • Submission online
  • Instruction for reviewer
  • Reviewer login
  • Office login
    • Contact
  • Tel: +86-024-83978208
    E-mail: jmst@imr.ac.cn
    Address: 72 Wenhua Road, Shenyang, Liaoning, 110016, China
    • WeChat
    • Copyright © Editorial Office of Journal of Materials Sciences and Technology, All Rights Reserved.