Abstract: Deformation-induced microstructures of high-Mn austenite steel was investigated by metallography,X-ray diffraction and SEM.The ε-martensite and slip-bands are deformation-in- duced on the{111} planes,and appear as thin straight laths with 60～80° alignment difference be- tween them.It was found that ε-martensite and slip bands are kinked at fcc twin boundaries with the kinked angle 35～40°.The bands of equilateral triangle in the microstructure of tensile deformation are presented.

Key words: deformation-induced microstructure, hcp epsilon martensite, slip-band, crystallography, high-Mn austenite steel