Microstructure and Properties of Cu-Cr-Zr Alloy after Rapidly Solidified Aging and Solid Solution Aging

Abstract

Abstract: The structure and properties of Cu-Cr-Zr alloy were studied after rapidly solidified aging and solid solution aging. At the early stage of aging (500℃ for 15 min), the hardness and the conductivity of the alloy rapidly solidified are 143 HV and 72% IACS, respectively. Under the same aging condition, the hardness and electrical conductivity of the alloy solid solution treated can reach 86 HV and 47% IACS, respectively. The microstructure was analyzed, and the grain size after rapid solidification is much smaller than that after solid solution treatment. By rapidly solidified aging the fine precipitates distribute inside the grains and along the grain boundary, while by solid solution aging there are large Cr particles along the grain boundary.

Key words: Cu-Cr-Zr alloy, Properties, Solid solution aging, Rapidly solidified aging

Ping LIU, Juanhua SU, Qiming DONG, Hejun LI. Microstructure and Properties of Cu-Cr-Zr Alloy after Rapidly Solidified Aging and Solid Solution Aging[J]. J Mater Sci Technol, 2005, 21(04): 475-478.

[1]	Xiaoxiao Li, Meiqiong Ou, Min Wang, Long Zhang, Yingche Ma, Kui Liu. Effect of boron addition on the microstructure and mechanical properties of K4750 nickel-based superalloy [J]. J. Mater. Sci. Technol., 2021, 60(0): 177-185.
[2]	Hong Sun, Nan Deng, Jianqiang Li, Gang He, Jiangtao Li. Highly thermal-conductive graphite flake/Cu composites prepared by sintering intermittently electroplated core-shell powders [J]. J. Mater. Sci. Technol., 2021, 61(0): 93-99.
[3]	Lin Yuan, Jiangtao Xiong, Yajie Du, Jin Ren, Junmiao Shi, Jinglong Li. Microstructure and mechanical properties in the TLP joint of FeCoNiTiAl and Inconel 718 alloys using BNi2 filler [J]. J. Mater. Sci. Technol., 2021, 61(0): 176-185.
[4]	Hui Jiang, Dongxu Qiao, Wenna Jiao, Kaiming Han, Yiping Lu, Peter K. Liaw. Tensile deformation behavior and mechanical properties of a bulk cast Al_0.9CoFeNi₂ eutectic high-entropy alloy [J]. J. Mater. Sci. Technol., 2021, 61(0): 119-124.
[5]	Qin Xu, Dezhi Chen, Chongyang Tan, Xiaoqin Bi, Qi Wang, Hongzhi Cui, Shuyan Zhang, Ruirun Chen. NbMoTiVSi_x refractory high entropy alloys strengthened by forming BCC phase and silicide eutectic structure [J]. J. Mater. Sci. Technol., 2021, 60(0): 1-7.
[6]	B.N. Du, Z.Y. Hu, L.Y. Sheng, D.K. Xu, Y.X. Qiao, B.J. Wang, J. Wang, Y.F. Zheng, T.F. Xi. Microstructural characteristics and mechanical properties of the hot extruded Mg-Zn-Y-Nd alloys [J]. J. Mater. Sci. Technol., 2021, 60(0): 44-55.
[7]	Fu-Zhi Dai, Haiming Zhang, Huimin Xiang, Yanchun Zhou. Theoretical investigation on the stability, mechanical and thermal properties of the newly discovered MAB phase Cr₄AlB₄ [J]. J. Mater. Sci. Technol., 2020, 39(0): 161-166.
[8]	Bin Hu, Xin Tu, Haiwen Luo, Xinping Mao. Effect of warm rolling process on microstructures and tensile properties of 10￢ﾀﾉMn steel [J]. J. Mater. Sci. Technol., 2020, 47(0): 131-141.
[9]	Qi Wang, Wen Shi, Bo Zhu, Dang Sheng Su. An effective and green H₂O₂/H₂O/O₃ oxidation method for carbon nanotube to reinforce epoxy resin [J]. J. Mater. Sci. Technol., 2020, 40(0): 24-30.
[10]	Kui Wang, Jingfeng Wang, Xiaoxu Dou, Yuanding Huang, Norbert Hort, Sarkis Gavras, Shijie Liu, Yanwu Cai, Jinxing Wang, Fusheng Pan. Microstructure and mechanical properties of large-scale Mg-Gd-Y-Zn-Mn alloys prepared through semi-continuous casting [J]. J. Mater. Sci. Technol., 2020, 52(0): 72-82.
[11]	Kritesh Kumar Gupta, Tanmoy Mukhopadhyay, Aditya Roy, Sudip Dey. Probing the compound effect of spatially varying intrinsic defects and doping on mechanical properties of hybrid graphene monolayers [J]. J. Mater. Sci. Technol., 2020, 50(0): 44-58.
[12]	Boon Teoh Tan, Shunnian Wu, Franklin Anariba, Ping Wu. A DFT study on brittle-to-ductile transition of D0₂₂-TiAl₃ using multi-doping and strain-engineered effects [J]. J. Mater. Sci. Technol., 2020, 51(0): 180-192.
[13]	Lei Liu, Liang Wu, Xiaobo Chen, Deen Sun, Yuan Chen, Gen Zhang, Xingxing Ding, Fusheng Pan. Enhanced protective coatings on Ti-10V-2Fe-3Al alloy through anodizing and post-sealing with layered double hydroxides [J]. J. Mater. Sci. Technol., 2020, 37(0): 104-113.
[14]	Hanghang Liu, Paixian Fu, Hongwei Liu, Yanfei Cao, Chen Sun, Ningyu Du, Dianzhong Li. Effects of Rare Earth elements on microstructure evolution and mechanical properties of 718H pre-hardened mold steel [J]. J. Mater. Sci. Technol., 2020, 50(0): 245-256.
[15]	Sharafadeen Kunle Kolawole, Wang Hai, Shuyuan Zhang, Ziqing Sun, Muhammad Ali Siddiqui, Ihsan Ullah, Wei Song, Frank Witte, Ke Yang. Preliminary study of microstructure, mechanical properties and corrosion resistance of antibacterial Ti-15Zr-xCu alloy for dental application [J]. J. Mater. Sci. Technol., 2020, 50(0): 31-43.

Microstructure and Properties of Cu-Cr-Zr Alloy after Rapidly Solidified Aging and Solid Solution Aging

RichHTML

PDF (PC)

Knowledge

Abstract

Cite this article

share this article

References

Related Articles 15

Recommended Articles

Metrics

Comments