Abstract: 3-dimensional reticulated ceramics (3DRCs) and their same composition ceramic disks (SCCDs) were fabricated by sol-gel method, with the composition of SrO·6Fe2O3(30%), SiC(35%) and TiO2(35%), sintered at 1200℃ in N2. The dielectric and magnetic parameters of such 3DRCs and their SCCDs were measured respectively in a temperature range from room temperature to 800℃ and in a frequency range from 2.6 GHz to 18 GHz. The results showed that the dielectric and magnetic loss of 3DRCs were obviously larger than those of their SCCDs in a wide range of temperature and the whole range of measuring frequency. The increase of dielectric loss of 3DRCs was much higher than that of magnetic loss compared to their SCCDs, which was found due to the 3D net structure extrinsic characteristics.

Key words: 3-dimentional reticulated ceramics, Dielectric loss, Magnetic loss, Extrinsic loss.