Abstract: The study for the interface of as-grown diamond and metallic film surrounding diamond is an attractive way for understanding diamond growth mechanism at high temperature and high pressure (HTHP), because it is that through the interface carbon atom groups from the molten film are transported to growing diamond surface. It is of great interest to perform atomic force microscopy (AFM) experiment, which provides a unique technique different from that of normal optical and electron microscopy studies, to observe the interface morphology. In the present paper, we report first that the morphologies obtained by AFM on the film are similar to those of corresponding diamond surface, and they are the remaining traces after the carbon groups moving from the film to growing diamond. The fine particles and a terrace structure with homogeneous average step height are respectively found on the diamond (100) and (111) surface. Diamond growth conditions show that its growth rates and the temperature gradients in the boundary layer of the molten film at HTHP result in the differences of surface morphologies on diamond planes, being rough on (100) plane and even on the (111) plane. The diamond growth on the (100) surface at HPHT could be considered as a process of unification of these diamond fine particles or of carbon atom groups recombination on the growing diamond crystal surface. Successive growth layer steps directly suggest the layer growth mechanism of the diamond (111) plane. The sources of the layer steps might be two-dimensional nuclei and dislocations.

Key words: Synthetic diamond, High temperature and high pressure, Metallic film, AFM