Abstract: The rolling treatment of steel-mushy QTi3.5-3.5 graphite composite was conducted under different relative reduction at room temperature. The effect of room-temperature rolling on interfacial mechanical property of steel-mushy QTi3.5-3.5 graphite composite was studied and the relationship between interfacial shear strength and relative reduction was established. The results show that, for steel-mushy QTi3.5-3.5 graphite composite, which consists of 1.2 mm-thick 08Al steel plate and 2.8 mm-thick QTi3.5-3.5 graphite layer, there is a nonlinear relationship between interfacial shear strength and relative reduction in graphite layer. When relative reduction is smaller than 1.1%, interfacial shear strength increases with increasing the relative reduction. When relative reduction is larger than 1.1%, interfacial shear strength decreases with increasing the relative reduction. When relative reduction is 1.1%, the largest interfacial shear strength of 145.2 MPa can be obtained.

Key words: Rolling, Relative reduction, Interfacial shear strength, Steel-mushy Cu-graphite composite