J. Mater. Sci. Technol. ›› 2008, Vol. 24 ›› Issue (03): 309-312.

• 论文 • 上一篇    下一篇

Effects of Mo and Zr on Microstructure, Mechanical Properties and Wear Resistance of Fe-Al Based Alloys

I.D.Yeo, T.Y.Ra, H.S.Kim, H.J.Bang, Y.G.Yoo, W.Y.Kim   

  • 收稿日期:1900-01-01 修回日期:1900-01-01 出版日期:2008-05-28 发布日期:2009-10-10

Effects of Mo and Zr on Microstructure, Mechanical Properties and Wear Resistance of Fe-Al Based Alloys

I.D.Yeo, T.Y.Ra, H.S.Kim, H.J.Bang, Y.G.Yoo, W.Y.Kim   

  1. Advanced Materials R&D Division, Korea Institute of Industrial Technology, 7-47, Songdo-dong, Yeonsu-gu, Incheon 406-800, South Korea
  • Received:1900-01-01 Revised:1900-01-01 Online:2008-05-28 Published:2009-10-10
  • Contact: I.D.Yeo

RichHTML

0

PDF (PC)

997

Abstract: In this work the microstructure, mechanical properties and wear resistance of Fe-Al based alloys with various alloying elements were studied. The microstructures were examined by optical and scanning electron microscopy (SEM) equipped with an energy dispersive X-ray spectroscope (EDS). Two types of alloys were prepared by vacuum arc melting. One is Fe-28Al based alloys (D03 structured) with and without alloying elements such as Mo and Zr. The other one is Fe-35Al based alloys (B2 structured) produced with the same manner. For both types of alloys, Mo addition had found to exhibit an equiaxed microstructure, while dendritic structure was observed to show the effect of Zr addition. These microstructural features were more evinced with increasing content of alloying element. Concerning the mechanical properties and wear resistance, Fe-35Al based alloys were superior to Fe-28Al based alloys over the whole temperature range investigated.

Key words: Fe-Al alloy, Intermetallic, Mechanical properties, Wear resistance