Structure and Magnetic Properties of Fe_(76.5)Si_(13.5)B_9Cu_1 Alloy with Nanoscale Grain Size

Fei ZHOU; Kaiyuan HE; Lizhi CHENG and Zuhan LAI(Dept. of Materials Science and Engineering, Northeastern University, Shenyang, 110006, China)( Dept. of Phys., Northeastern University)   

  • 收稿日期:1994-11-28 修回日期:1994-11-28 出版日期:1994-11-28 发布日期:2009-10-10

Structure and Magnetic Properties of Fe_(76.5)Si_(13.5)B_9Cu_1 Alloy with Nanoscale Grain Size

Fei ZHOU; Kaiyuan HE; Lizhi CHENG and Zuhan LAI(Dept. of Materials Science and Engineering, Northeastern University, Shenyang, 110006, China)( Dept. of Phys., Northeastern University)   

  • Received:1994-11-28 Revised:1994-11-28 Online:1994-11-28 Published:2009-10-10

RichHTML

0

PDF (PC)

500

摘要： l.IntroductionNanocrystalline(NC)materialsaresingle-ormulti-phasepolycrystalsinwhichthecrysta1sizeisintheorderofnanometers,norma1lyJ-5Onm.SincethefirstreportbyG1eiterandhiscollaborators[l],suchmaterialshavebeenintensivelystudiedinbothstructuresandproperties.Recently,NCFe-Cu-Nb-Si-BsoftmagneticalloyshavebeendevelopedbyYoshizawaelal.[2,3].Thealloysarefirstformedintoamor-phousribbons,andthenanne....

Abstract: The structure and magnetic properties of Fe76.5Si13.5B9Cu1 alloys with a nanocrystalline (NC) bcc Fe(Si) phase trom about 23 to 46 nm in diameter, which were first formed into amorphous ribbons and then annealed at various temperatures between 703 and 773 K, have been investigated. At annealing temperatures from 703 to 748 K, the single NC bcc(Si) phase is obtained in the crystallized alloys. The grain size and the Si-content in the NC bcc Fe(Si) phase for the alloys annealed at different temperatures are presented. The soft magnetic properties and the saturation magnetostriction for the alloys with the NC bcc Fe(Si) phase are also measured. The results show that, the saturation magnetizotion and the permeability are improved for the alloys with only the NC bcc Fe(Si) phase and become better with decreasing of the NC bcc phase size, and the saturation magnetostriction declines for the alloys with increasing Si-content in the NC bcc Fe(Si) phase.