Formation of a new intermediate phase and its evolution toward θ' during aging of pre-deformed Al-Cu alloys

doi:10.1016/j.jmst.2018.11.022

材料科学与技术 ›› 2019, Vol. 35 ›› Issue (5): 885-890.DOI: 10.1016/j.jmst.2018.11.022

收稿日期:2018-04-30 接受日期:2018-08-29 出版日期:2019-05-10 发布日期:2019-02-20

Formation of a new intermediate phase and its evolution toward θ' during aging of pre-deformed Al-Cu alloys

Peipei Ma^a, Chunhui Liu^a^b^?(), Ziyao Ma^b, Lihua Zhan^a^b, Minghui Huang^a^b

^aLight Alloy Research Institute of Central South University, State Key Laboratory of High-Performance Complex Manufacturing, Central South University,Changsha, 410083, China
^bSchool of Mechanical and Electrical Engineering, Central South University, Changsha, 410083, China

Received:2018-04-30 Accepted:2018-08-29 Online:2019-05-10 Published:2019-02-20
Contact: Liu Chunhui
About author:
¹ These authors contribute equally to this paper.

摘要/Abstract

Abstract:

The frequent occurrence of hitherto unknown phase Pre-θ'-2 and unusual 1.5 c_θ' thick θ' precipitate was observed by atomic-resolution scanning transmission electron microscopy in the well-studied Al-Cu alloys. This phenomenon is associated with heterogeneous precipitate nucleation and growth on pre-existing dislocations introduced by slight deformation prior to aging. In this study, the precise structure details of Pre-θ'-2 was determined by atomic scale imaging, image simulation based on image forming theories and first principle calculations. Pre-θ'-2 has a well-defined ordered structure sandwiched between two 2a_Al (～1.5c_θ') spaced Cu layers on {200}_Al planes. The strong structural similarities between Pre-θ'-2 and 1.5 c_θ' thick θ' in terms of interfacial structure and thickness, coupled with energetic calculations and preliminary in-situ observations, lead us to propose a new precipitation path toward key strengthening phase θ'.

Key words: Aluminum alloys, Precipitation, Deformation, Age-hardening

. [J]. 材料科学与技术, 2019, 35(5): 885-890.

Peipei Ma, Chunhui Liu, Ziyao Ma, Lihua Zhan, Minghui Huang. Formation of a new intermediate phase and its evolution toward θ' during aging of pre-deformed Al-Cu alloys[J]. J. Mater. Sci. Technol., 2019, 35(5): 885-890.

图/表 8

Fig. 1 Age hardening curve at 165 ℃ for the Al-Cu alloy with and without pre-deformation.

Fig. 2 HAADF-STEM images showing the typical microstructure in the alloy aged at 165 ℃ for 9?h: (a) without pre-deformation; (b) overall mixed-precipitates morphology in pre-deformed sample; (c-g) high resolution images of the large precipitates marked by the arrows P1-P4, respectively, in (a); (e) a magnified image of the lower tip of P2. The electron beam is parallel to [001]Al direction.

Fig. 3 Atomic-resolution HAADF-STEM images of (a) pre-θ′-2 and (b) 1.5 cθ′ thick θ′. The yellow arrow points to an enlarged part of the precipitate indicated by the solid-line box. The atomic model and the simulated image are overlaid on the experimental image. Inset with dashed-line box shows a HAADF-STEM image reported in ref. [18] of the complex hetero-phase θ′′+ θt′ at the semi-coherent interface (rim region) between Al matrix and θ′ phase. A 1-nm-wide region of θ′′ is present at the rim area of each precipitate. The arrow at the rim interface represents a dislocation with Burgers vector (aAl/2) [100]. The electron beam is parallel to [001]Al direction.

Fig. 4 Calculated total energies of various proposed structures of Pre-θ'-2 with the first one as the most favorable one.

Fig. 5 Formation energy per Cu atom compared to Cu in solid solution of different precipitate structures appearing in Al-Cu alloy with pre-deformation. The energy of a pre-θ'-2 was set as the zero energy.

Fig. 6 TEM images showing the precipitates and dislocations in the pre-deformed Al-Cu alloy after ageing. The large precipitates normally exist near or at irregular dislocation segments marked by the arrows.

Fig. 7 HAADF-STEM images showing the typical microstructure in the pre-deformed high-purity Al-Cu alloy aged at 165 ℃ for 9?h: (a) overall mixed-precipitates morphology; (b-d) high resolution images of the large precipitates marked by the arrows P1-P3, respectively, in (a). The electron beam is parallel to [001]Al direction.

Fig. 8 Structural change from Pre-θ'-2 to θ' induced by e-beam exposure under TEM.

参考文献

[1]	A. Wilm, Metallurgie 8 (1911) 223.
[2]	M.G. Frank, W. Gayle, Science 266 (1994) 1015-1017.
[3]	L. Liu, J.H. Chen, S.B. Wang, C.H. Liu, S.S. Yang, C.L. Wu, Mater. Sci. Eng. A 606(2014) 187-195.
[4]	C.H. Liu, J. Chen, Y.X. Lai, D.H. Zhu, Y. Gu, J.H. Chen, Mater. Des. 87(2015) 1-5.
[5]	L.J.C. Bergers, J.T.M. De Hosson, M.G.D. Geers, J.P.M. Hoefnagels, Mater. Sci.Eng. A 722 (2018) 37-46.
[6]	M. Gazizov, R. Kaibyshev, Mater. Sci. Eng. A 702 (2017) 29-40.
[7]	S. Fu, Y. Zhang, H. Liu, D. Yi, B. Wang, Y. Jiang, Z. Chen, N. Qi, J. Mater.Sci.Technol. 34(2018) 335-343.
[8]	Z. Shen, Q. Ding, C. Liu, J. Wang, H. Tian, J. Li, Z. Zhang, J. Mater.Sci.Technol. 33(2017) 1159-1164.
[9]	T.F. Chung, Y.L. Yang, B.M. Huang, Z. Shi, J. Lin, T. Ohmura, J.R. Yang, ActaMater. 149(2018) 377-387.
[10]	J.M. Silcock, T.J. Heal, H.K. Hardy, J. Inst. Metals 82 (1954) 239-248.
[11]	G.D. Preston, Nature 142 (1938), 570-570.
[12]	L. Bourgeois, C. Dwyer, M. Weyland, J.F. Nie, B.C. Muddle, Acta Mater. 59(2011) 7043-7050.
[13]	S. Hu, M. Baskes, M. Stan, L. Chen, Acta Mater. 54(2006) 4699-4707.
[14]	V. Vaithyanathan, C. Wolverton, L.Q. Chen, Acta Mater. 52(2004) 2973-2987.
[15]	J.F. Nie, B.C. Muddle, Acta Mater. 56(2008) 3490-3501.
[16]	K.W.U. Dahmen, Phys. Status Solidi A 80 (1983) 249-262.
[17]	L. Bourgeois, C. Dwyer, M. Weyland, J.-F. Nie, B.C. Muddle, Acta Mater. 60(2012) 633-644.
[18]	L. Bourgeois, N.V. Medhekar, A.E. Smith, M. Weyland, J.F. Nie, C. Dwyer, Phys.Rev. Lett. 111(2013) 1-5, 046102.
[19]	B.A. Chen, G. Liu, R.H. Wang, J.Y. Zhang, L. Jiang, J.J. Song, J. Sun, Acta Mater. 61(2013) 1676-1690.
[20]	Y. Chen, M. Weyland, C.R. Hutchinson, Acta Mater. 61(2013) 5877-5894.
[21]	C. Liu, S.K. Malladi, Q. Xu, J. Chen, F.D. Tichelaar, X. Zhuge, H.W. Zandbergen,Sci. Rep. 7(2017) 1-8, 2184.
[22]	Y. Chen, Z. Zhang, Z. Chen, A. Tsalanidis, M. Weyland, S. Findlay, L.J. Allen, J. Li,N.V. Medhekar, L. Bourgeois, Acta Mater. 125(2017) 340-350.
[23]	Y. Yang, L. Zhan, Q. Ma, J. Feng, X. Li, J. Mater. Sci.Technol. 229(2016) 697-702.
[24]	C.H. Liu, Z.Y. Ma, P.P. Ma, L.H. Zhan, M.H. Huang, Mater. Sci. Eng. A 733 (2018)28-38.
[25]	P.P. Ma, C.H. Liu, C.L. Wu, L.M. Liu, J.H. Chen, Mater. Sci. Eng. A 676 (2016)138-145.
[26]	C. Koch, Arizona State University, 2002.
[27]	J.F.G. Kresse, Phys. Rev. B 54 (1996) 11169-11186.
[28]	J.F.G. Kresse, Comput. Mat. Sci. 6(1996) 15-50.
[29]	J.H.G. Kresse, J. Phys. Condens. Matter 6 (1994) 8245-8257.
[30]	S.J. Pennycook, Ultramicroscopy 30 (1989) 58-69.
[31]	S.Q. Wang, M. Schneider, H.Q. Ye, G. Gottstein, Scr. Mater. 51(2004) 665-669.
[32]	H. Liu, B. Bellón, J. Llorca, Acta Mater. 132(2017) 611-626.
[33]	Y.L. Zhao, W.W. Hu, Z.Q. Yang, Micron 76 (2015) 1-5.
[34]	Y. Xin, T. Ma, X. Ju, J. Qiu, J. Mater.Sci.Technol. 29(2013) 467-470.

Formation of a new intermediate phase and its evolution toward θ' during aging of pre-deformed Al-Cu alloys

RichHTML

PDF (PC)

可视化

摘要/Abstract

引用本文

使用本文

图/表 8

参考文献

相关文章 0

编辑推荐

Metrics

本文评价