Improved distortion prediction in additive manufacturing using an experimental-based stress relaxation model
Ruishan Xie, Qingyu Shi, Gaoqiang Chen
Table 1
Values of
A
and
n
at different temperatures.
Temperature (℃)
A
n
600
5.37 × 10
-27
6.47
700
2.13 × 10
-29
8.22
800
7.31 × 10
-23
7.16