Multi-scale crystal plasticity finite element simulations of the microstructural evolution and formation mechanism of adiabatic shear bands in dual-phase Ti20C alloy under complex dynamic loading

Yu Zhou^a^,^b, Qunbo Fan^a^,^b^,^c^,^*(

), Xin Liu^a^,^b, Duoduo Wang^a^,^b^,^c, Xinjie Zhu^a^,^b^,^c, Kai Chen^a^,^b^,^c

Fig. 6.. Effective plastic strain and effective stress contour maps of the dual-phase multiple grains: (a, c, e, g) effective plastic strain and (b, d, f, h) effective stress at ε_T = 0.02, 0.025, 0.04, and 0.10, respectively.