The effect of crack tip environment on crack growth behaviour of a low alloy steel at cathodic potentials in artificial seawater
Yong Lia, Zhiyong Liua,b,*(
), Endian Fana, Zhongyu Cuic, Jinbin Zhaoa,d
), Endian Fana, Zhongyu Cuic, Jinbin Zhaoa,d
.
Fig. 3.. Fracture morphologies of E690 steel during the crack growth process in (a) air and (b) artificial seawater.