Designing new work-hardenable ductile Ti-based multilayered bulk metallic glass composites with ex-situ and in-situ hybrid strategy

Shifeng Lin, Zhengwang Zhu, Shaofan Ge, Long Zhang, Dingming Liu, Yanxin Zhuang, Huameng Fu, Hong Li, Aimin Wang, Haifeng Zhang

Table 2 Tensile properties of the ML-BMGCs with adding different Nb contents.

Sample Yield strength (MPa) Ultimate strength (MPa) Fracture strength (MPa) Plasticity (%) Nb2 1396 ± 10 1416 ± 2 1416 ± 5 0.46 ± 0.1 Nb5 1197 ± 10 1331 ± 2 1300 ± 5 4.33 ± 0.1 Nb8 1078 ± 10 1221 ± 2 1112 ± 5 5.10 ± 0.1