Microstructural evolution and FCC twinning behavior during hot deformation of high temperature titanium alloy Ti65
Zhixin Zhanga,c, Jiangkun Fana,b,*(), Bin Tanga,b, Hongchao Koua,b, Jian Wangc, Xin Wangc, Shiying Wangd, Qingjiang Wange, Zhiyong Chene, Jinshan Lia,b,*()

.

Fig. 7.. KAM maps of Ti65 alloy deformed at 960℃and 0.1 s-1 with different true strain (a) 0.04, (b) 0.4, (c) 0.7 and (d) KAM histogram.