Microstructural evolution and FCC twinning behavior during hot deformation of high temperature titanium alloy Ti65
Zhixin Zhanga,c, Jiangkun Fana,b,*(), Bin Tanga,b, Hongchao Koua,b, Jian Wangc, Xin Wangc, Shiying Wangd, Qingjiang Wange, Zhiyong Chene, Jinshan Lia,b,*()

.

Fig. 6.. Schmid factors (SF) histogram of α phase with Basal < a>, Prismatic < a> and Pyramidal < a> slip systems for Ti65 alloy deformed at 960 ℃ and 0.1 s-1 with different true strain: (a) 0.04; (b) 0.4; (c) 0.7.