Microstructural evolution and FCC twinning behavior during hot deformation of high temperature titanium alloy Ti65
Zhixin Zhanga,c, Jiangkun Fana,b,*(
), Bin Tanga,b, Hongchao Koua,b, Jian Wangc, Xin Wangc, Shiying Wangd, Qingjiang Wange, Zhiyong Chene, Jinshan Lia,b,*()
), Bin Tanga,b, Hongchao Koua,b, Jian Wangc, Xin Wangc, Shiying Wangd, Qingjiang Wange, Zhiyong Chene, Jinshan Lia,b,*()
.
Fig. 15.. (a) (b) TEM images of Ti65 alloy deformed at 960 ℃ (0.1 s-1) with 0.7 strain and (c) corresponding EDS results of silicide in (b). (d) (e) TEM images deformed at 1080 ℃ (0.1 s-1) with 0.7 strain and (f) the SAED pattern of FCC twins highlighted in (e). The SAED patterns corresponding to the TEM images are embedded in the picture respectively.