Zhixin Zhang a,c, Jiangkun Fan a,b,*( ), Bin Tang a,b, Hongchao Kou a,b, Jian Wang c, Xin Wang c, Shiying Wang d, Qingjiang Wang e, Zhiyong Chen e, Jinshan Li a,b,*( )
|
Fig. 14.. Grain boundary contrast maps with true strain (a) 0.04, (b) 0.4, (c) 0.7 and recrystallized maps with true strain (e) 0.4, (f) 0.7 for Ti65 alloy deformed at 1080 ℃and 0.1 s-1 and (d) statistical diagram of misorientation angle.
|