Deformation twinning in equiaxed-grained Fe-6.5 wt.%Si alloy after rotary swaging
Chaoyu Hana, Shibo Wena, Feng Yea,*(
), Wenjia Wub, Shaowei Xuea, Yongfeng Lianga, Binbin Liua, Junpin Lina
), Wenjia Wub, Shaowei Xuea, Yongfeng Lianga, Binbin Liua, Junpin Lina
.
Fig. 3.. Microstructures of the Fe-6.5 wt.% Si ally specimens at 300 °C after tensile after heat treatment at 800 °C × 10 min: necking area (a) and homogeneous deformation area (b) after SQ, necking area (c) and homogeneous deformation area (d) after BQ.