Deformation twinning in equiaxed-grained Fe-6.5 wt.%Si alloy after rotary swaging

Chaoyu Han, Shibo Wen, Feng Ye, Wenjia Wu, Shaowei Xue, Yongfeng Liang, Binbin Liu, Junpin Lin

Table 6 Euler angles and TTSF value in {112}<111> twinning system after BQ.

Grain Euler angles TTSF Grain Euler angles TTSF 1 (224.6 24.2 25.8) 0.44 25 (208.1 11.3 43.5) 0.50 2 (318.3 34.8 71.0) 0.33 26 (197.1 22.9 41.4) 0.37 3 (219.1 41.4 54.7) 0.41 27 (210.9 31.1 51.0) 0.45 4 (81.1 43.2 60.6) 0.43 28 (303.7 21.6 78.3) 0.46 5 (254.3 38.4 69.4) 0.42 29 (187.9 51.8 47.5) 0.19 6 (73.4 24.4 53.7) 0.44 30 (179.5 36.9 57.1) 0.33 7 (73.1 30.5 64.5) 0.4 31 (32.1 28.2 68.0) 0.45 8 (234.3 46.7 36.0) 0.24 32 (183.3 12.9 3.0) 0.43 9 (93.0 42.4 77.5) 0.28 33 (222.7 38.2 25.9) 0.40 10 (290.9 51.5 48.6) 0.19 34 (12.6 33.8 27.9) 0.36 11 (354.3 33.9 46.3) 0.30 35 (248.6 26.8 14.0) 0.40 12 (240.6 20.3 54.3) 0.47 36 (110.3 23.7 27.4) 0.44 13 (302.8 29.9 81.1) 0.42 37 (175.9 15 63.2) 0.41 14 (65.7 33.4 41.8) 0.4 38 (265.3 36 4.6) 0.34 15 (16.0 22.6 37.6) 0.45 39 (14.2 52.5 49.3) 0.19 16 (137.3 14.5 85.5) 0.42 40 (197.7 36.4 43.0) 0.30 17 (358.9 36.9 37.1) 0.29 41 (180.3 16.4 80.2) 0.48 18 (48.1 28.7 83.9) 0.41 42 (139.8 44.1 42.2) 0.23 19 (79.4 29.6 35.4) 0.40 43 (33.9 36.6 5.9) 0.42 20 (35.9 19.0 39.2) 0.47 44 (183.0 44.7 57.6) 0.26 21 (34.6 19.5 42.3) 0.39 45 (139.0 42.7 34.3) 0.35 22 (58.4 48.5 40.7) 0.19 46 (79.6 29.3 36.8) 0.42 23 (65.7 33.4 41.8) 0.34 47 (13.8 29.2 35.0) 0.39 24 (235.6 20.7 23.1) 0.46 48 (249.9 47.6 42.0) 0.22