Deformation twinning in equiaxed-grained Fe-6.5 wt.%Si alloy after rotary swaging
|
Chaoyu Han, Shibo Wen, Feng Ye, Wenjia Wu, Shaowei Xue, Yongfeng Liang, Binbin Liu, Junpin Lin
|
|
|
Table 5 Euler angles and TTSF value in {112}<111> twinning system after SQ.
|
|
Grain | Euler angles | TTSF | Grain | Euler angles | TTSF | 1 | (254.7 | 27.1 | 47.1) | 0.41 | 34 | (27.2 | 21.8 | 49.2) | 0.46 | 2 | (55.8 | 37.1 | 22.4) | 0.34 | 35 | (140.3 | 49.3 | 33.1) | 0.22 | 3 | (258.5 | 41.7 | 1.9) | 0.28 | 36 | (204.6 | 29.5 | 69.2) | 0.40 | 4 | (252.2 | 25.5 | 84.7) | 0.43 | 37 | (186.8 | 19.1 | 44.4) | 0.30 | 5 | (123.3 | 49.7 | 48.7) | 0.21 | 38 | (317.2 | 13.0 | 66.6) | 0.49 | 6 | (300.0 | 40.6 | 5.4) | 0.44 | 39 | (10.2 | 6.5 | 24.1) | 0.28 | 7 | (279.7 | 40.6 | 4.3) | 0.29 | 40 | (26.3 | 9.7 | 41.4) | 0.32 | 8 | (346.6 | 22.5 | 67.0) | 0.45 | 41 | (281.2 | 15.6 | 11.6) | 0.49 | 9 | (265.4 | 28.3 | 69.7) | 0.41 | 42 | (349.3 | 39.6 | 16.0) | 0.48 | 10 | (256.0 | 30.2 | 46.1) | 0.38 | 43 | (258.2 | 23.6 | 9.1) | 0.45 | 11 | (240.1 | 23.5 | 10.7) | 0.45 | 44 | (8.5 | 35.8 | 35.6) | 0.33 | 12 | (88.7 | 13.0 | 5.6) | 0.49 | 45 | (209.3 | 44.4 | 3.8) | 0.42 | 13 | (150.4 | 22.8 | 9.9) | 0.45 | 46 | (30.7 | 39.2 | 11.6) | 0.40 | 14 | (321.5 | 22.0 | 42.7) | 0.45 | 47 | (167.8 | 3.5 | 52.5) | 0.32 | 15 | (51.0 | 27.2 | 26.0) | 0.41 | 48 | (181.2 | 43.6 | 49.2) | 0.26 | 16 | (28.7 | 26.3 | 26.9) | 0.42 | 49 | (255.6 | 21.6 | 67.8) | 0.46 | 17 | (227.5 | 38.5 | 56.3) | 0.31 | 50 | (355.9 | 38.1 | 60.2) | 0.32 | 18 | (1.2 | 52.0 | 48.8) | 0.19 | 51 | (295.2 | 32.0 | 53.0) | 0.36 | 19 | (89.8 | 52.7 | 47.4) | 0.18 | 52 | (3.9 | 22.4 | 38.3) | 0.39 | 20 | (296.3 | 18.3 | 88.6) | 0.47 | 53 | (7.1 | 36.2 | 5.4) | 0.48 | 21 | (19.5 | 36.4 | 48.8) | 0.32 | 54 | (142.3 | 9.4 | 61.7) | 0.33 | 22 | (156.4 | 17.2 | 13.9) | 0.48 | 55 | (62.8 | 38.5 | 41.2) | 0.28 | 23 | (60.5 | 33.6 | 43.9) | 0.34 | 56 | (75.7 | 47.1 | 26.9) | 0.23 | 24 | (69.5 | 31.9 | 19.3) | 0.38 | 57 | (50.1 | 46.4 | 63.4) | 0.25 | 25 | (276.4 | 43.4 | 88.7) | 0.26 | 58 | (220.6 | 30.0 | 44.1) | 0.47 | 26 | (220.7 | 18.9 | 34.1) | 0.47 | 59 | (290.9 | 4.8 | 34.9) | 0.38 | 27 | (270.8 | 9.2 | 64.2) | 0.50 | 60 | (339.9 | 26.7 | 44.5) | 0.41 | 28 | (134.3 | 43.8 | 26.8) | 0.28 | 61 | (125.8 | 23.4 | 74.3) | 0.45 | 29 | (27.1 | 36.4 | 42.4) | 0.31 | 62 | (206.2 | 40.6 | 33.2) | 0.40 | 30 | (321.2 | 31.8 | 64.4) | 0.38 | 63 | (207.2 | 31.8 | 24.1) | 0.38 | 31 | (235.3 | 1.4 | 86.2) | 0.48 | 64 | (279.9 | 41.6 | 24.9) | 0.43 | 32 | (55.1 | 29.1 | 21.7) | 0.40 | 65 | (290.5 | 25.0 | 20.3) | 0.43 | 33 | (104.4 | 29.6 | 84.0) | 0.40 | 66 | (193.0 | 17.2 | 34.2) | 0.30 |
|
|
|