Phase transformation and structural evolution in a Ti-5at.% Al alloy induced by cold-rolling
Bingqiang Weia, Song Nia, Yong Liua, Xiaozhou Liaob, Min Songa,*()

.

Fig. 5.. (a) A bright-field TEM image of the R60 sample for the HCP matrix, with the inset being an SAED pattern obtained from the area outlined by a red dotted circle. (b) A dark-field TEM image of (a) using the reflection marked by the red circle in the inset of (a). (c) A bright-field TEM image of the R60 sample for the FCC structure and the inset is a corresponding SAED pattern. (d) The grain size distribution of the FCC structure in the R60 sample.