Haoqiang Zhanga,b, Lin Liua,b, Zhiliang Peia, Nanlin Shia, Jun Gonga, Chao Suna,*()

.

Fig. 4.. Morphologies of composites fabricated in 900 °C/50 MPa/2 h with 15 mg/cm2 (a), 900 °C/50 MPa/2 h with 30 mg/cm2 (b), 900 °C/50 MPa/2 h with 45 mg/cm2 (c), 900 °C/60 MPa/2 h with 30 mg/cm2 (d), 900 °C/70 MPa/2 h with 30 mg/cm2 (e), 900 °C/80 MPa/2 h with 30 mg/cm2 (f).