Effect of warm rolling process on microstructures and tensile properties of 10￢ﾀﾉMn steel
Bin Hua, Xin Tua, Haiwen Luoa,b,*(
), Xinping Maob
), Xinping Maob
.
Fig. 6.. EBSD band contrast images overlapped by phase distribution on microstructures of specimens after the IA at 620°C for 5 h, when they were warm rolled at 250°C (a), 600°C (b), 650°C (c) and 750°C (d, e) by 50% reduction in thickness, or at 600°C (f, g) and 650°C (h) by 63%. (e) and (g) are the magnified views of marked regions in (d) and (f); (e1) and (e2) are the AES mapping of C and Mn concentrations in the marked region of (e). The green and the deep red represent austenite and cementite respectively.