The authors regret to inform that (i) a wrong Table 1 was uploaded, and a corrected one was show below; (ii) a reference label is missing in caption of Fig. 8(A), and it should be: Fig. 8. Interfacial evolution between nanozones and lamellar zones during thermal exposure: (A) as-deposited state [45]; (B) 20 h; (C) 500 h; (iii) a wrong figure was uploaded in Fig. 2(A, 0 h), and a revised one is shown below.
Table 1 Parameters used for plasma spraying.
Parameters | Nano | HOSP |
---|---|---|
Plasma arc voltage / V | 60 | 60 |
Plasma arc current / A | 650 | 700 |
Flow rate of primary gas (Ar) / L·min-1 | 80 | 45 |
Flow rate of secondary gas (H2) / L·min-1 | 16 | 7 |
Spray distance / mm | 110 | 80 |
Torch traverse speed / mm·s-1 | 500 | 500 |
Fig. 2 Global structural evolution during thermal exposure: (A) conventional TBCs; (B) nanostructured TBCs [45].
The authors would like to apologize for the inconvenience caused.
/
〈 | 〉 |