Influence of Temperature on Stacking Fault Energy and Creep Mechanism of a Single Crystal Nickel-based Superalloy

Tian Sugui,Zhu Xinjie,Wu Jing,Yu Huichen,Shu Delong,Qian Benjiang

Fig. 6. Dislocation configuration within the γ′ phase after alloy crept for 133?h up to fracture at 1070?°C/160?MPa: (a) g?=?022, (b) g?=?002, (c) g ?=?020, (d) g=0 2 ? 2.