Influence of Temperature on Stacking Fault Energy and Creep Mechanism of a Single Crystal Nickel-based Superalloy

Tian Sugui,Zhu Xinjie,Wu Jing,Yu Huichen,Shu Delong,Qian Benjiang

Fig. 4. Dislocation configuration within the γ′ phase after alloy crept for 241?h up to fracture at 760?°C/810?MPa: (a)g?=?002, (b) g ?=?020, (c)g= 1 ˉ 13 .