Influence of Temperature on Stacking Fault Energy and Creep Mechanism of a Single Crystal Nickel-based Superalloy

Tian Sugui,Zhu Xinjie,Wu Jing,Yu Huichen,Shu Delong,Qian Benjiang

Fig. 3. Microstructures after the alloy crept up to fracture under different conditions: (a) 760?°C/810?MPa, (b) 980?°C/300?MPa, (c) 1070?°C/160?MPa.