材料科学与技术. 2016, 32 (10): 1003-1007 doi: 10.1016/j.jmst.2016.08.018

High Temperature Stress Rupture Anisotropy of a Ni-Based Single Crystal Superalloy

Wang Guanglei,Liu Jinlai,Liu Jide,Jin Tao,Sun Xiaofeng,Sun Xudong,Hu Zhuangqi

Fig. 2. Two-beam TEM bright field images on cross section of the (a) [001] oriented specimen, (b) [011] oriented specimen and [111] oriented specimen (c) after 2 h deformation and (d) after rupture at 900 °C/445 MPa.