Fe-3%Si电工钢铸坯柱状晶织构的演变规律*
付勇军1,2,杨平1(
),蒋奇武2,王晓达2,金文旭2
),蒋奇武2,王晓达2,金文旭2
EVOLUTION OF TEXTURES OF COLUMNAR GRAINS IN Fe-3%Si ELECTRICAL STEEL SLABS
Yongjun FU1,2,Ping YANG1(),Qiwu JIANG2,Xiaoda WANG2,Wenxu JIN2
),Qiwu JIANG2,Xiaoda WANG2,Wenxu JIN2
图6. 47%压下率冷轧及再结晶退火后样品的EBSD取向成像图及ODF截面图(j2 =45°)
Fig.6. EBSD orientation maps (a1~c1) and ODF sections (j2=45°) (a2~c2) of samples after cold rolling with 47% reduction and recrystallization annealing
(a1, a2) single columnar grain (b1, b2) double columnar grains (c1, c2) multi-columnar grains