Fe-3%Si电工钢铸坯柱状晶织构的演变规律*
付勇军1,2,杨平1(
),蒋奇武2,王晓达2,金文旭2
),蒋奇武2,王晓达2,金文旭2
EVOLUTION OF TEXTURES OF COLUMNAR GRAINS IN Fe-3%Si ELECTRICAL STEEL SLABS
Yongjun FU1,2,Ping YANG1(),Qiwu JIANG2,Xiaoda WANG2,Wenxu JIN2
),Qiwu JIANG2,Xiaoda WANG2,Wenxu JIN2
图1. 单、双和多柱状晶的EBSD取向成像图及{001}极图
Fig.1. EBSD orientation maps (a1~c1) and {001} pole figures (a2~c2) of initial columnar grains in three samples (ND—normal direction, RD—rolling direction, TD—transverse direction)
(a1, a2) single columnar grain (b1, b2) double columnar grains (c1, c2) multi-columnar grains