Fe-3%Si电工钢铸坯柱状晶织构的演变规律*
付勇军1,2,杨平1(
),蒋奇武2,王晓达2,金文旭2
),蒋奇武2,王晓达2,金文旭2
EVOLUTION OF TEXTURES OF COLUMNAR GRAINS IN Fe-3%Si ELECTRICAL STEEL SLABS
Yongjun FU1,2,Ping YANG1(),Qiwu JIANG2,Xiaoda WANG2,Wenxu JIN2
),Qiwu JIANG2,Xiaoda WANG2,Wenxu JIN2
图8. 单柱状晶主要取向的变化趋势
Fig.8. Variation trend to the content of grains with main orientations for single columnar grain (1—columnar, 2—primary cold rolling, 3—recrystallization annealing, 4—secondary cold rolling, 5—recrystallization annealing, 6—secondary recrystallization annealing)