Annealing-induced Hardening in a Nanostructured Low-carbon Steel Prepared by Using Dynamic Plastic Deformation
L.X. Sun1, N.R. Tao1,*, M. Kuntz2, J.Q. Yu3, K. Lu1
Fig. 3 Typical cross-sectional TEM bright-#cod#x0fb01;eld images of DPD samples after annealing at 673 K for 20 min a and b and the distribution thickness of lamellar structures measured from TEM bright-#cod#x0fb01;eld images c.