Fatigue Behaviors of a Ni-free ZrCuFeAlAg Bulk Metallic Glass in Simulated Body Fluid
Wang Yimei, Liu Yan, Liu Lin* 
Fatigue Behaviors of a Ni-free ZrCuFeAlAg Bulk Metallic Glass in Simulated Body Fluid |
|
Wang Yimei, Liu Yan, Liu Lin
|
| Fig. 3. SEM fractograph of a crack profile on the side surface of a specimen which was subjected to the corrosion-fatigue test prior to failure in a stress range of 1000 MPa after 4800 cycles. The arrow above indicates the crack propagation direction. |
| |