Analysis of Surface Oxide Films Formed in Hydrogenated Primary Water on Alloy 690TT Samples With Different Surface States
Zhiming Zhang, Jianqiu Wang
, En-Hou Han, Wei Ke
, En-Hou Han, Wei Ke 
Analysis of Surface Oxide Films Formed in Hydrogenated Primary Water on Alloy 690TT Samples With Different Surface States |
|
Zhiming Zhang, Jianqiu Wang
, En-Hou Han, Wei Ke |
| Fig. 9 TEM images from surfaces of oxide films a ground to 400 grit and b EP; and 1 O, 2 Cr, 3 Ni, and 4 Fe EDS mapping of the same oxide films grown on Alloy 690TT after 60 days' immersion in 1500 #cod#x000D7; 10-6 B and 2.3 #cod#x000D7; 10-6 Li solution with 2.5 #cod#x000D7; 10-6 H2 at 325 #cod#x000b0;C and 15.6 MPa |
| |