Analysis of Surface Oxide Films Formed in Hydrogenated Primary Water on Alloy 690TT Samples With Different Surface States
Zhiming Zhang, Jianqiu Wang
, En-Hou Han, Wei Ke
, En-Hou Han, Wei Ke 
Analysis of Surface Oxide Films Formed in Hydrogenated Primary Water on Alloy 690TT Samples With Different Surface States |
|
Zhiming Zhang, Jianqiu Wang
, En-Hou Han, Wei Ke |
| Fig. 8 a Cross-sectional TEM image of the oxide film grown on Alloy 690TT ground to 400 grit after 60 days' immersion in 1500 #cod#x000D7; 10-6 B and 2.3 #cod#x000D7; 10-6 Li solution with 2.5 #cod#x000D7; 10-6 H2 at 325 #cod#x000b0;C and 15.6 MPa, b a magnified view of the area marked by a rectangle in a. |
| |