CVD SiC Fiber Electrochemically Treated by AC Current

Kun LUO, Nanlin SHI, Yapei ZU   

  • Received:1900-01-01 Revised:1900-01-01 Online:2003-05-28 Published:2009-10-10
  • Contact: Kun LUO

Abstract: The tensile strength of CVD SiC fiber was remarkably improved by electrochemical surface treatment. SEM analyses reveal that AC current treatment could form a more compact and complete SiO2 layer than DC current on the surface of the SiC fiber, which was beneficial to the improvement of tensile strength. It was also verified that AC current was more effective for producing high performance SiC fiber with SiO2 surface layer than DC current. The frequency is a sensitive parameter for the process; but the signals of input current had relatively small effect on the tensile strength of SiC fiber. A further discussion for this phenomenon was completed. The proposed operational parameters are 0.3 A, 5 kHz of sine wave and 91 m/h of the receiving rate respectively.

Key words: SiC fiber, Electrochemical treatment, AC current