Preparation and characterization of BAS reinforced with SiC platelets

Jiancun RAO, Jiancheng GU, Yu ZHOU, Feng YE, Tingquan LEI   

  1. Harbin Institute of Technology, Harbin 150001, China
  • Received:1999-08-12 Revised:1999-10-26 Online:2000-09-28 Published:2009-10-10
  • Contact: Jiancun RAO

Abstract: BAS glass-ceramic powders were prepared by sol-gel processing. SiC platelets reinforced BAS glass-ceramic matrix composites with high density and uniform microstructure could be made using hot-pressing method. The related processing parameters were studied in this work, including effects of additional seed on transformation from H to M of barium aluminosilicate. DTA method was used to determine exact time to press mixture powders during hot-pressing for the purpose of effective densification. Microstructure and mechanical properties of the composites were investigated by mean of SEM, XRD and TEM techniques as well as three points bending test and single edge notched beam measurement. The results showed that the flexural strength and fracture toughness value of the BAS glass-ceramic matrix composites could be effectively improved by the addition of the SiC platelets. But the relative densities of composites were slightly decreased. The main toughening mechanism is crack deflection, platelets' pull-out and bridging. The increased value of flexural strength is contributed to the load transition effect from matrix to SiC platelets.

Key words: