J Mater Sci Technol ›› 2000, Vol. 16 ›› Issue (03): 277-280.

• Research Articles • Previous Articles     Next Articles

Synthesis, microstructure and optical absorption of coatings with doping of nano-TiO2 for protection against ultraviolet irradiation

Ye ZHANG, Lide ZHANG, Chimei MO, Yuanhong LI, Lianzeng YAO, Weili CAI   

  1. Institute of Solid State Physics, Chinese Academy of Sciences, Hefei 230031, China...
  • Received:1999-03-26 Revised:1999-05-21 Online:2000-05-28 Published:2009-10-10
  • Contact: Lide ZHANG

Abstract: The synthesis of dispersions of MMA (methylmethacrylate) with different concentrations of oleic acid coated nano-TiO2 particles was performed by hydrolysis of TiCl4 in the mixture solutions of MMA, oleic acid and H2O with various concentrations. When MMA :oleic acid : H2O : TiCl4 1.00 : 0.064 : 0.01 : 0.032 (by mol fraction), the dispersion of MMA with oleic acid coated nano-TiO2 particles was very stable. Optical absorption result showed that the absorption band was located in the ultraviolet range from 200 to 400 nm. This dispersion was added to a kind of automobile surface lustering agent (type II), and then this lustering agent with nano-TiO2 was coated on the surface of automobile surface paint. When the doping amount of the dispersion in the lustering agent=10 vol. pet, the state of paint (color and glossiness) did not present any change after irradiation of an ultraviolet lamp with the power of 1000 watt for two days. The sample with surface paint and lustering agent doped by 10 percent dispersion after suffering from irradiation of the sunlight for half a year (from May to November) kept the original state. However, for the samples with automobile paint and lustering agent without doping of nano-TiO2, the color and glossiness lost easily after irradiation of an ultraviolet lamp. These results prove that nano-TiO2 is a kind of high-efficient additive of paint for protection against ultraviolet irradiation.

Key words: