Abstract: Commercial grain oriented silicon steel was cold rolled to thickness from 0.06 to 0.10 mm by cross shear rolling, then annealed in vacuum or a hydrogen atmosphere furnace. Deformation textures of the sheets were researched by ODF method and reverse pole figure quantitative analyses. The results indicate that: in the condition of the cross shear rolling, the deformation texture of roiled sheet is generally similar to that of conventional rolled sheet, however, the texture distribution through the thickness is asymmetrical. With mismatch speed ratio increasing, the amount of Goss texture increases, With reduction ratio increasing, the intensity of gamma-fiber becomes strong.